Annealing Temperature Dependence of ZTO Thin Film Properties and Its Application on Thin Film Transistors by Inkjet Printing

被引：0
|
作者：
Sang Ouk Ryu
Cheul Ho Ha
Ho Young Jun
Si Ok Ryu
机构：
[1] Dankook University,Department of Electronics and Electrical Engineering
[2] Yeungnam University,School of Chemical Engineering
来源：
Journal of Electronic Materials | 2020年 / 49卷
关键词：
Zinc tin oxide; thin film; thin film transistor; inkjet-printer; solution-based process;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, inkjet-printed zinc tin oxide:Cl (ZTO:Cl) thin films were analyzed using x-ray diffraction, x-ray photoelectron spectroscopy (XPS) and all the films were annealed at temperatures ranging from 100°C to 600°C. XPS analysis showed that the formation of metal-oxide bonds in the films was complete with annealing temperatures at or above 500°C. Furthermore, inkjet-printed thin film transistors (TFTs) were examined using scanning electron microscopy and current–voltage characteristic measurements. The ZTO:Cl TFTs performed best when annealed at 500°C. The average carrier mobility and the on/off ratio were found to be 2.71 cm2/V s and 1.82 × 107, respectively.
引用
收藏
页码：2003 / 2007
页数：4
相关论文
共 50 条
  • [1] Annealing Temperature Dependence of ZTO Thin Film Properties and Its Application on Thin Film Transistors by Inkjet Printing
    Ryu, Sang Ouk
    Ha, Cheul Ho
    Jun, Ho Young
    Ryu, Si Ok
    JOURNAL OF ELECTRONIC MATERIALS, 2020, 49 (03) : 2003 - 2007
  • [2] Inkjet printing of sustainable ZTO/AlOx thin film transistors
    Moreira, Pedro Gabriel
    Martins, Rodrigo
    Carlos, Emanuel
    Branquinho, Rita
    FLEXIBLE AND PRINTED ELECTRONICS, 2024, 9 (04):
  • [3] Effect of Annealing Temperature on Electrical Properties of ZTO Thin-Film Transistors
    Wang, Chong
    Guo, Liang
    Lei, Mingzhou
    Wang, Chao
    Chu, Xuefeng
    Yang, Fan
    Gao, Xiaohong
    Wamg, Huan
    Chi, Yaodan
    Yang, Xiaotian
    NANOMATERIALS, 2022, 12 (14)
  • [4] Inkjet printing of polymer thin film transistors
    Kawase, T
    Shimoda, T
    Newsome, C
    Sirringhaus, H
    Friend, RH
    THIN SOLID FILMS, 2003, 438 : 279 - 287
  • [5] Process optimization of inkjet printing for organic thin-film transistors
    Han, Kyung Tai
    Song, Dae Ho
    Choi, Min Hee
    Choi, Dae Lim
    Sautter, Armin
    Jang, Jin
    IDW '06: PROCEEDINGS OF THE 13TH INTERNATIONAL DISPLAY WORKSHOPS, VOLS 1-3, 2006, : 727 - +
  • [6] All-polymer thin film transistors fabricated by inkjet printing
    Kawase, T
    Sirringhaus, H
    Friend, RH
    Shimoda, T
    ORGANIC FIELD EFFECT TRANSISTORS, 2001, 4466 : 80 - 88
  • [7] Thin film deposition, patterning, and printing in organic thin film transistors
    Ling, MM
    Bao, ZN
    CHEMISTRY OF MATERIALS, 2004, 16 (23) : 4824 - 4840
  • [8] Materials System for Inkjet Printing High Performance Thin-Film Transistors
    Zhang, Qi
    Xiang, Huiqing
    Liu, Jianguo
    Zeng, Xiaoyan
    PROGRESS IN CHEMISTRY, 2019, 31 (10) : 1417 - 1424
  • [9] Inkjet Printed Electrodes in Thin Film Transistors
    Tao, Ruiqiang
    Ning, Honglong
    Chen, Jianqiu
    Zou, Jianhua
    Fang, Zhiqiang
    Yang, Caigui
    Zhou, Yicong
    Zhang, Jianhua
    Yao, Rihui
    Peng, Junbiao
    IEEE JOURNAL OF THE ELECTRON DEVICES SOCIETY, 2018, 6 (01): : 774 - 790
  • [10] Dependence of Mobility on the Temperature in Organic Thin Film Transistors
    Li, Na
    Zeng, Jiawei
    Luo, Zhi
    Deng, Wanling
    2019 IEEE INTERNATIONAL CONFERENCE ON ELECTRON DEVICES AND SOLID-STATE CIRCUITS (EDSSC), 2019,
12345