F-doped TiO2 microporous coating on titanium with enhanced antibacterial and osteogenic activities

To enhance bacterial resistance and osteogenesis of titanium (Ti) -based implants, TiO2/calcium-phosphate coatings (TiCP) doped with various amounts of fluorine (F) (designated as TiCP-F1, TiCP-F6, and TiCP-F9) were prepared on Ti by micro-arc oxidation. The F doped TiCP coatings possess a microporous structure (pore size of 3–4 μm in average diameter) which is evenly covered by nano-grains of 30–60 nm in size. Successful F incorporation into TiCP was determined by X-ray photoelectron spectroscopy, and it shows weak influence on the microstructure, phase compositions, surface roughness and wettability of TiCP. All the coatings bonded firmly to the Ti substrates and showed enduring high adhesion strength in biological circumstances. The bacterial resistance and osteogenesis of the coatings were evaluated by implanting testing materials in vitro and in an infected rabbit model caused by bacteria. Both the in vitro and in vivo results indicated that TiCP and TiCP-F1 were of much higher osteogenic activity compared with Ti but lacking of bacterial resistance, whereas TiCP with high F addition (TiCP-F6 and TiCP-F9) exhibited both dramatically improved bacterial resistance and osteogenesis. In summary, TiCP-F6 possessed the best antibacterial and osteogenic activities, especially exhibited excellent osseointegration efficacy in the infected rabbit model.