Structure, optical and magnetic properties of new Bi0.5Na0.5TiO3- SrMnO3−δ solid solution materials

The new Bi0.5Na0.5TiO3-SrMnO3−δ solid solution materials were fabricated via sol–gel method. The random incorporation of Sr and Mn cations into host lattice of Bi0.5Na0.5TiO3 resulted in structural distortion and influenced on the reduction of the optical band gap from 3.07 eV to 1.81 eV for pure Bi0.5Na0.5TiO3 and 9 mol% SrMnO3−δ solid solution into Bi0.5Na0.5TiO3. The magnetic properties of Bi0.5Na0.5TiO3 materials at room temperature were tuned via compensation of diamagnetic material with weak-ferromagnetism to ferromagnetism with low SrMnO3−δ content and combination of paramagnetism/antiferromagnetism-like and ferromagnetism with higher SrMnO3−δ content solid solution in Bi0.5Na0.5TiO3. The tunable magnetic and optical properties of lead-free ferroelectric materials was promising for their application to green electronic devices.