Early stages hydration of high initial strength Portland cementPart II. NCDTA and Vicat analysis

This work complements a quantitative thermogravimetric study of the first 24 h of hydration of a high initial strength and sulphate resistant Portland cement (HS SR PC) using non-conventional differential thermal analysis (NCDTA) and Vicat needle method. Different water/cement (W/C) ratios from 0.35 to 0.85 were used to evaluate the most indicated operating conditions to maximize calcium hydroxide production for further use in CO2 capture. Thermogravimetric analysis data performed at 4 and 24 h of hydration were also compared to the NCDTA and Vicat data for each kind of paste, to analyze the influence of the W/C ratio on the simultaneous hydration and setting process. The increase of the W/C ratio increases the induction time retards the solidification and setting processes but increases the hydration degree as the W/C ratio is increased from 0.45. At 24 h, products prepared with 0.35 W/C ratio present a little higher hydration degree than those prepared with W/C = 0.45, because of the highest level of temperature in the reacting mixture in the former case, during the first 8 h. There is a practical limit of W/C = 0.66 to prepare the pastes, due to a limit of the miscibility between HS SR PC and water, above which, the excess of water forms a separated phase that does not interfere in the hydration process.