Phase equilibrium data and liquidus for the system “MnO”-CaO-(Al2O3 + SiO2) at Al2O3/SiO2 = 0.41

被引：0
|
作者：
Ghasem Roghani
Evgueni Jak
Peter Hayes
机构：
[1] The University of Queensland,PYROSEARCH, Pyrometallurgy Research Centre, School of Engineering
来源：
Metallurgical and Materials Transactions B | 2002年 / 33卷
关键词：
Material Transaction; Gehlenite; Dicalcium Silicate; Pseudowollastonite; Pseudoternary Section;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Phase-equilibrium data and the liquidus for the system “MnO”-CaO-(Al2O3-SiO2) at a manganese-rich alloy saturation have been determined in the temperature range from 1423 to 1723 K. The results are presented in the form of a pseudoternary section “MnO”-CaO-(Al2O3 + SiO2) with an Al2O3/SiO2 weight ratio of 0.41. The following primary phases are present in the range of conditions investigated: 3Al2O3·2SiO2; SiO2; MnO·Al2O3·2SiO2; (Mn,Ca)O·SiO2; 2(Mn,Ca)O·SiO2; MnO·Al2O3; (Mn,Ca)O; α-2CaO·SiO2; α′-2CaO·SiO2; 2CaO·Al2O3·SiO2; CaO·SiO2, and CaO·Al2O3·2SiO2. The presence of alumina in this system is shown to have a significant effect on the liquidus compared to the system “MnO”-CaO-SiO2, leading to the stabilization of the anorthite and gehlenite phases.
引用
收藏
页码：839 / 849
页数：10
相关论文
共 50 条
  • [1] Phase equilibrium data and liquidus for the system "MnO"-CaO-(Al2O3+SiO2) at Al2O3/SiO2=0.41
    Roghani, G
    Jak, E
    Hayes, P
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2002, 33 (06): : 839 - 849
  • [2] Phase-equilibrium data and liquidus for the system “MnO”-CaO-Al2O3-SiO2 at Al2O3/SiO2 of 0.55 and 0.65
    Ghasem Roghani
    Evgueni Jak
    Peter Hayes
    Metallurgical and Materials Transactions B, 2003, 34 : 173 - 182
  • [3] Phase-equilibrium data and liquidus for the system "MnO"-CaO-Al2O3-SiO2 at Al2O3/SiO2 of 0.55 and 0.65
    Roghani, G
    Jak, E
    Hayes, P
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2003, 34 (02): : 173 - 182
  • [4] AMPHOTERIC CHARACTER OF AL2O3 IN THE SYSTEM CAO AL2O3 SIO2
    NGUYEN, VL
    SILIKATY, 1989, 33 (04): : 357 - 365
  • [5] Thermodynamic properties of liquid phase in the CaO•SiO2-CaO•Al2O3•2SiO2-2CaO•Al2O3•SiO2 system
    Fabrichnaya, OB
    Nerád, I
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2000, 20 (04) : 505 - 515
  • [6] Effect of Al2O3/SiO2 and CaO/Al2O3 ratios on wettability and structure of CaO–SiO2–Al2O3-based mold flux system
    Wan-lin Wang
    Er-zhuo Gao
    Le-jun Zhou
    Lei Zhang
    Huan Li
    Journal of Iron and Steel Research International, 2019, 26 : 355 - 364
  • [7] The Melting Temperature of CaO-(2CaO•SiO2)-B2O3-SiO2-(Al2O3) Slag System
    Wang, Hong-ming
    Li, Pei-si
    Li, Gui-rong
    Zhang, Mian
    Zhao, Zhao
    Zhao, Yutao
    ADVANCED MATERIALS AND PROCESS TECHNOLOGY, PTS 1-3, 2012, 217-219 : 35 - 38
  • [8] Viscosity of SiO2-CaO-Al2O3 Slag with Low Silica - Influence of CaO/Al2O3, SiO2/Al2O3 Ratio
    Siafakas, Dimitrios
    Matsushita, Taishi
    Jarfors, Anders Eric Wollmar
    Hakamada, Shinya
    Watanabe, Masahito
    ISIJ INTERNATIONAL, 2018, 58 (12) : 2180 - 2185
  • [9] Activities of Aluminum and Calcium Oxides in the CaO–Al2O3 and CaO–SiO2–Al2O3 Melts
    V. N. Nevidimov
    Yu. M. Durina
    S. A. Krasikov
    E. M. Zhilina
    A. S. Bykov
    Russian Metallurgy (Metally), 2022, 2022 : 134 - 141
  • [10] Activities of Aluminum and Calcium Oxides in the CaO–Al2O3 and CaO–SiO2–Al2O3 Melts
    Nevidimov, V.N.
    Durina, Yu. M.
    Krasikov, S.A.
    Zhilina, E.M.
    Bykov, A.S.
    Russian Metallurgy (Metally), 2022, 2022 (02) : 134 - 141
12345