Effects of Cr addition on glass-forming ability and mechanical properties of Cu–Zr–Al bulk metallic glass

Effects of a small amount addition of Cr on glass-forming ability (GFA) and mechanical properties of Cu–Zr–Al bulk metallic glass were investigated. The GFA of (Cu46Zr46Al8)100−xCrx (x = 0, 0.25, 0.5, 0.75, and 1 at%) alloys tends to decrease with the increasing Cr content. A good correlation between the GFA and the temperature interval of supercooled liquid region ΔTx or parameter γ exists in these alloys. Addition of an appropriate amount of Cr can significantly improve the plasticity of the alloys. The bulk metallic glass with x = 0.5 exhibits promising mechanical properties with high fracture strength of 1870 MPa and obvious plastic strain of 2.23%.