Mechanical Behavior of Sandwich Composites Under Three-Point Bending Fatigue

被引：0
|
作者：
K. Bey
K. Tadjine
R. Khelif
A. Chemami
M. Benamira
Z. Azari
机构：
[1] Laboratoire de Mécanique Industrielle,
[2] Département de Génie Mécanique,undefined
[3] Université Badji Mokhtar BP 12 Annaba 23000,undefined
[4] Laboratoire de Recherche en Risque Industriel/CND et Sécurité de Fonctionnement,undefined
[5] Département de Génie Mécanique,undefined
[6] Université Badji Mokhtar BP 12 Annaba 23000,undefined
[7] Laboratoire de Mécanique,undefined
[8] Biomécanique,undefined
[9] Polymère,undefined
[10] Structures (LaBPS)-ENIM,undefined
来源：
Mechanics of Composite Materials | 2015年 / 50卷
关键词：
sandwich; three-point bending; fatigue modulus; damage;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The mechanical behavior of sandwich composite materials in fatigue loading is investigated. Fatigue tests in three-point bending were conducted on two types of sandwich materials, [04] and [0/902/0]. The rupture mode observed on tested specimens showed a debond between the core and skins, as well as cracks in the core at 45∙ to the neutral axis of sandwich. Degradation of the rigidity modulus in fatigue was determined from the deflection equation for the two sandwiches. The experiments revealed that the modulus of the [04] sandwich degraded faster than that of [0/902/0]. The evolution of shear modulus in fatigue of both sandwiches is also described analytically using exponential and polynomial models.
引用
收藏
页码：747 / 756
页数：9
相关论文
共 50 条
  • [1] Mechanical Behavior of Sandwich Composites Under Three-Point Bending Fatigue
    Bey, K.
    Tadjine, K.
    Khelif, R.
    Chemami, A.
    Benamira, M.
    Azari, Z.
    [J]. MECHANICS OF COMPOSITE MATERIALS, 2015, 50 (06) : 747 - 756
  • [2] EXPERIMENTAL INVESTIGATION OF THE MECHANICAL BEHAVIOR OF HONEYCOMB SANDWICH COMPOSITE UNDER THREE-POINT BENDING FATIGUE
    Mzad, Hocine
    [J]. MATERIALS PHYSICS AND MECHANICS, 2022, 48 (02): : 217 - 231
  • [3] Deformation and Failure Behavior of Wooden Sandwich Composites with Taiji Honeycomb Core under a Three-Point Bending Test
    Hao, Jingxin
    Wu, Xinfeng
    Oporto, Gloria
    Wang, Jingxin
    Dahle, Gregory
    Nan, Nan
    [J]. MATERIALS, 2018, 11 (11):
  • [4] Nonlinear behavior of composite sandwich beams in three-point bending
    E. E. Gdoutos
    I. M. Daniel
    K.-A. Wang
    J. L. Abot
    [J]. Experimental Mechanics, 2001, 41 : 182 - 189
  • [5] Nonlinear behavior of composite sandwich beams in three-point bending
    Gdoutos, EE
    Daniel, IM
    Wang, KA
    Abot, JL
    [J]. EXPERIMENTAL MECHANICS, 2001, 41 (02) : 182 - 189
  • [6] Static three-point bending behavior of aluminum foam sandwich
    Zu, Guoyin
    Song, Binna
    Zhong, Zhaoyang
    Li, Xiaobing
    Mu, Yongliang
    Yao, Guangchun
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 540 : 275 - 278
  • [7] Nonlinear behavior of composite sandwich beams in three-point bending
    Gdoutos, EE
    Daniel, IM
    Wang, KA
    Abot, JL
    [J]. PROCEEDINGS OF THE SEM IX INTERNATIONAL CONGRESS ON EXPERIMENTAL MECHANICS, 2000, : 155 - 158
  • [8] Static behavior of three-dimensional integrated core sandwich composites subjected to three-point bending
    Karahan, Mehmet
    Gul, Hakan
    Karahan, Nevin
    Ivens, Jan
    [J]. JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2013, 32 (09) : 664 - 678
  • [9] Crack kinking in sandwich structures under three-point bending
    Theotokoglou, E. E.
    Tourlomousis, I. I.
    [J]. THEORETICAL AND APPLIED FRACTURE MECHANICS, 2010, 53 (02) : 158 - 164
  • [10] Behavior of CFRC/Al Foam Composite Sandwich Beams under Three-Point Bending
    Vcelka, Martin
    Dunn, Michelle
    Durandet, Yvonne
    Berndt, Christopher C.
    Ruan, Dong
    [J]. ADVANCED ENGINEERING MATERIALS, 2014, 16 (01) : 9 - 14
12345