Water cleaning ability and local structure of iron-containing soda-lime silicate glass

A relationship between waste-water cleaning ability and local structure of iron-containing soda-lime silicate glass, 15Na2O·15CaO·xFe2O3·(70-x)SiO2 (x = 10–50 in mass%), abbreviated as NCFSx glass, was investigated by means of 57Fe-Mössbauer spectroscopy, redox titration with KMnO4 for the determination of chemical oxygen demand (COD) and inductively coupled plasma optical emission spectroscopy (ICP-OES). Mössbauer spectra of NCFSx glass with “x” of 10 and 30 were composed of two doublets: one due to FeIIIO4 tetrahedra (Td) with isomer shift (δ) of 0.23–0.26 mm s − 1 and quadrupole splitting (Δ) 1.01–1.04 mm s − 1, and the other due to FeIIO6 octahedra (Oh) with δ of 1.00–1.03 mm s − 1 and Δ of 2.03–2.05 mm s − 1. Absorption area for FeII(Td) was decreased from 9.7 to 6.5 and 0.0 % when “x” was increased from 10 to 30 and 50. A leaching test performed with 500 mL of artificial waste water and 2.0 g of NCFS50 revealed waste-water cleaning ability of soda-lime glass, e.g., COD was reduced from 280 to 55.2 mg L − 1 after 10 day-leaching. After 10 day-leaching, it proved that iron was dissolved into waste water to a level of 5.3\documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \setlength{\oddsidemargin}{-69pt} \begin{document}$_{7} \times 10^{-1}$\end{document} mg L − 1. These results prove that organic matter could be effectively decomposed with iron-containing soda-lime silicate glass.