Plastic instability during creep deformation of a NiAl-Hf single-crystal alloy—A case study

被引:0
|
作者
A. Garg
S. V. Raj
R. D. Noebe
M. V. Nathal
R. Darolia
机构
[1] AYT Corp. working at NASA-Lewis Research Center,the Advanced Metallics Branch
[2] NASA-Lewis Research Center,undefined
[3] General Electric Aircraft Engines,undefined
关键词
Material Transaction; Shear Band; Gage Section; Rupture Life; Plastic Instability;
D O I
暂无
中图分类号
学科分类号
摘要
Tensile samples from NiAl-Hf single crystals, having the same nominal composition and heat treated and creep tested under identical conditions at 1144 K, were found to exhibit very different rupture lives and creep ductilities. A case study was conducted on two samples with creep rupture lives of 343.6 and 37.0 hours (with corresponding creep ductilities of 12.3 and 39.9 pct, respectively) in order to find the causes of such a large variation in creep properties. Detailed microstructural analyses using optical microscopy, scanning electron microscopy (SEM), and transmission electron microscopy (TEM) indicated that the sample with higher rupture life and lower ductility had deformed uniformly along the length of the gage section, whereas the sample with lower rupture life and higher ductility (sample L) deformed by localized plastic deformation resulting in shear failure. This shear failure was due to a plastic instability in sample L which was caused by the presence of a high density of large Hf-rich interdendritic particles that were formed during casting of the single-crystal ingot but did not go into solution during the homogenization heat treatment. The role of these particles in causing nonuniform deformation, which led to strain localization and a premature failure in sample L, has been described in detail.
引用
收藏
页码:179 / 189
页数:10
相关论文
共 50 条
  • [1] Plastic instability during creep deformation of a NiAl-Hf single-crystal alloy - A case study
    Garg, A
    Raj, SV
    Noebe, RD
    Nathal, MV
    Darolia, R
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (01): : 179 - 189
  • [2] Effect of Si on the microstructure and stability of different phases in a NiAl-Hf single-crystal alloy
    Garg, A
    Noebe, RD
    Locci, IE
    Darolia, R
    ELECTRON MICROSCOPY 1998, VOL 2: MATERIALS SCIENCE 1, 1998, : 151 - 152
  • [3] PLASTIC DEFORMATION OF SINGLE-CRYSTAL NIAL
    WASILEWSKI, RJ
    BUTLER, SR
    HANLON, JE
    TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME, 1967, 239 (09): : 1357 - +
  • [4] Crystallography of the NiHfSi phase in a NiAl (0.5Hf) single-crystal alloy
    Garg, A
    Noebe, RD
    Darolia, R
    ACTA MATERIALIA, 1996, 44 (07) : 2809 - 2820
  • [5] STUDY OF PLASTIC-DEFORMATION OF SINGLE-CRYSTAL TERBIUM
    CHUPYATOVA, LP
    CHUPRIKOV, GE
    PROKHOROVA, ON
    RUSSIAN METALLURGY, 1974, (06): : 128 - 130
  • [6] ASYMMETRIC CREEP DEFORMATION OF A SINGLE-CRYSTAL SUPERALLOY
    PAN, LM
    SCHEIBLI, I
    HENDERSON, MB
    MCLEAN, M
    ACTA METALLURGICA ET MATERIALIA, 1995, 43 (04): : 1375 - 1384
  • [7] Plastic Deformation of Single-Crystal Diamond Nanopillars
    Regan, Blake
    Aghajamali, Alireza
    Froech, Johannes
    Toan Trong Tran
    Scott, John
    Bishop, James
    Suarez-Martinez, Irene
    Liu, Ying
    Cairney, Julie M.
    Marks, Nigel A.
    Toth, Milos
    Aharonovich, Igor
    ADVANCED MATERIALS, 2020, 32 (09)
  • [8] THE MECHANISMS OF PLASTIC RELAXATION IN SINGLE-CRYSTAL DEFORMATION
    JACKSON, PJ
    MATERIALS SCIENCE AND ENGINEERING, 1986, 81 (1-2): : 169 - 174
  • [9] Element Distribution and Deformation Characteristics of a Single-crystal Nickel-based Alloy During High-temperature Creep
    Zhao G.
    Liu L.
    Tian N.
    Tian S.
    Fang Y.
    Yan H.
    Wang G.
    Cailiao Daobao/Materials Reports, 2022, 36 (04):
  • [10] A facility for plastic deformation of germanium single-crystal wafers
    Lebech, B
    Theodor, K
    Breiting, B
    Kealey, PG
    Hauback, B
    Lebech, J
    Sorensen, SA
    Clausen, KN
    PHYSICA B, 1997, 241 : 204 - 206