Corrosion of environmentally friendly lanthanum conversion coating on AA2024-T3 aluminum alloy

被引：0
|
作者：
R. Shoja Gharabagh
A. Sabour Rouhaghdam
机构：
[1] Tarbiat Modares University,Department of Materials Science, Faculty of Engineering
来源：
Protection of Metals and Physical Chemistry of Surfaces | 2014年 / 50卷
关键词：
Polarization Curve; Electrochemical Impedance Spectroscopy; Conversion Coating; Saturated Calomel Reference Electrode; Coated Alloy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this work, lanthanum conversion coating applied on AA2024-T3 aluminum alloy. The coatings were analyzed by optical and scanning electron microscope. The composition and phase structure of the coating were evaluated by EDS and XRD, respectively. Corrosion properties of the coating were investigated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization techniques. To explain the corrosion behavior of the coating, equivalent circuit was developed from the measurements. Results showed that the coating has a nanocrystaline structure with crystal size less than 50 nm which is composed of La2O3. Additionally, EIS measurements showed that the lanthanum conversion coating was monolayer. Measurements taken by polarization tests showed that the coating increased corrosion potential and decreased corrosion current density approximately one order of magnitude.
引用
收藏
页码：88 / 93
页数：5
相关论文
共 50 条
  • [1] Corrosion of environmentally friendly lanthanum conversion coating on AA2024-T3 aluminum alloy
    Gharabagh, R. Shoja
    Rouhaghdam, A. Sabour
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2014, 50 (01) : 88 - 93
  • [2] Interactions of the components of chromate conversion coating with the constituents of aluminum alloy AA2024-T3
    Chidambaram, D
    Clayton, CR
    Halada, GP
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2004, 151 (03) : B151 - B159
  • [3] Chemistry of a chromate conversion coating on aluminum alloy AA2024-T3 probed by vibrational spectroscopy
    Xia, L
    McCreery, RL
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1998, 145 (09) : 3083 - 3089
  • [4] Investigation of pretreatment effects on the formation of lanthanum based conversion coating on AA2024-T3
    R. Shoja Gharabagh
    A. Sabour Rouhaghdam
    Protection of Metals and Physical Chemistry of Surfaces, 2017, 53 : 112 - 117
  • [5] Investigation of Pretreatment Effects on the Formation of Lanthanum based Conversion Coating on AA2024-T3
    Gharabagh, R. Shoja
    Rouhaghdam, A. Sabour
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2017, 53 (01) : 112 - 117
  • [6] Effective corrosion protection of aluminum alloy AA2024-T3 with novel thin nanostructured oxide coating
    Merisalu, Maido
    Aarik, Lauri
    Kozlova, Jekaterina
    Mandar, Hugo
    Tarre, Aivar
    Sammelselg, Vaino
    SURFACE & COATINGS TECHNOLOGY, 2021, 411
  • [7] Inhibition of corrosion on AA2024-T3 by new environmentally friendly rare earth organophosphate compounds
    Forsyth, M.
    Markley, T.
    Ho, D.
    Deacon, G. B.
    Junk, P.
    Hinton, B.
    Hughes, A.
    CORROSION, 2008, 64 (03) : 191 - 197
  • [8] Influence of buffering on the spontaneous deposition of cerium conversion coatings for corrosion protection of AA2024-T3 aluminum alloy
    Stephan V. Kozhukharov
    Olaia F. Acuña
    Maria. S. Machkova
    Vladimir S. Kozhukharov
    Journal of Applied Electrochemistry, 2014, 44 : 1093 - 1105
  • [9] Influence of buffering on the spontaneous deposition of cerium conversion coatings for corrosion protection of AA2024-T3 aluminum alloy
    Kozhukharov, Stephan V.
    Acuna, Olaia F.
    Machkova, Maria. S.
    Kozhukharov, Vladimir S.
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2014, 44 (10) : 1093 - 1105
  • [10] Corrosion behaviour of AA2024-T3 anodized in tartaric sulphuric acid and sealed in environmentally friendly solutions
    Carangelo, A.
    Acquesta, A.
    Monetta, T.
    Bellucci, F.
    Curioni, M.
    METALLURGIA ITALIANA, 2017, (7-8): : 83 - 86
12345