Effect of Rhenium Addition on Hot Corrosion Resistance of Ni-Based Single Crystal Superalloys

被引：0
|
作者：
J. X. Chang
D. Wang
X. G. Liu
L. H. Lou
J. Zhang
机构：
[1] College of Materials Science and Engineering,Superalloys Division
[2] Xiʼan Shiyou University,Shenyang National Laboratory for Materials Science
[3] Institute of Metal Research,undefined
[4] Chinese Academy of Sciences,undefined
[5] Institute of Metal Research,undefined
[6] Chinese Academy of Sciences,undefined
来源：
Metallurgical and Materials Transactions A | 2018年 / 49卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Hot corrosion behavior of two Ni-based single crystal superalloys containing 0 Re and 2 wt pct Re in molten sodium sulfate (Na2SO4) at 900 °C in static air has been investigated using the “deposit recoat” method. It was shown that the incubation period of the Re-containing alloy was much longer than that of the Re-free alloy. It was because Re increased the stability of the chromium oxide (Cr2O3) scale, promoted the formation of nickel titanate (NiTiO3), and suppressed the diffusion of Ni. In addition, the overall corrosion kinetics of the Re-containing alloy followed a multistage parabolic law, compared with the Re-free alloy. This could be because Re increased the activity of chromium (Cr) and titanium (Ti), which resulted in the periodically opening and closure of the cracks in the outer oxide layer.
引用
收藏
页码：4343 / 4352
页数：9
相关论文
共 50 条
  • [1] Effect of Rhenium Addition on Hot Corrosion Resistance of Ni-Based Single Crystal Superalloys
    Chang, J. X.
    Wang, D.
    Liu, X. G.
    Lou, L. H.
    Zhang, J.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (09): : 4343 - 4352
  • [2] Effect of crystallographic orientation on the corrosion resistance of Ni-based single crystal superalloys
    Yang, Yanqiu
    Wen, Zhixun
    Zhao, Yanchao
    Wang, Jiapo
    Li, Zhenwei
    Yue, Zhufeng
    CORROSION SCIENCE, 2020, 170 (170)
  • [3] Role of Rhenium in Single Crystal Ni-based Superalloys
    Jin, Tao
    Wang, Wenzhen
    Sun, Xiaofeng
    Hu, Zhuangqi
    THERMEC 2009, PTS 1-4, 2010, 638-642 : 2257 - 2262
  • [4] Effects of Ru Addition on the Microstructures of the Ni-Based Single Crystal Superalloys
    Du Yunling
    Niu Jianping
    Wang Xinguang
    Liu Jinlai
    Liu Jide
    Zhou Yizhou
    Jin Tao
    Sun Xiaofeng
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (04) : 1248 - 1253
  • [5] Unveiling the Re effect in Ni-based single crystal superalloys
    Wu, Xiaoxiang
    Makineni, Surendra Kumar
    Liebscher, Christian H.
    Dehm, Gerhard
    Mianroodi, Jaber Rezaei
    Shanthraj, Pratheek
    Svendsen, Bob
    Buerger, David
    Eggeler, Gunther
    Raabe, Dierk
    Gault, Baptiste
    NATURE COMMUNICATIONS, 2020, 11 (01)
  • [6] Unveiling the Re effect in Ni-based single crystal superalloys
    Xiaoxiang Wu
    Surendra Kumar Makineni
    Christian H. Liebscher
    Gerhard Dehm
    Jaber Rezaei Mianroodi
    Pratheek Shanthraj
    Bob Svendsen
    David Bürger
    Gunther Eggeler
    Dierk Raabe
    Baptiste Gault
    Nature Communications, 11
  • [7] THERMAL CYCLING CREEP RESISTANCE OF Ni-BASED SINGLE CRYSTAL SUPERALLOYS
    Cormier, Jonathan
    PROCEEDINGS OF THE 13TH INTENATIONAL SYMPOSIUM OF SUPERALLOYS (SUPERALLOYS 2016), 2016, : 385 - 394
  • [8] On Crystal Mosaicity in Single Crystal Ni-Based Superalloys
    Hallensleben, Philipp
    Scholz, Felicitas
    Thome, Pascal
    Schaar, Helge
    Steinbach, Ingo
    Eggeler, Gunther
    Frenzel, Jan
    CRYSTALS, 2019, 9 (03):
  • [9] Mechanism of adding rhenium to improve hot corrosion resistance of nickel-based single-crystal superalloys
    Yang, Fang-Min
    Lian, Li-Xian
    Liu, Ying
    Gong, Xiu-Fang
    RARE METALS, 2021, 40 (08) : 2076 - 2082
  • [10] Mechanism of adding rhenium to improve hot corrosion resistance of nickel-based single-crystal superalloys
    Fang-Min Yang
    Li-Xian Lian
    Ying Liu
    Xiu-Fang Gong
    Rare Metals, 2021, 40 : 2076 - 2082
12345