Fracture mechanism of a thermal barrier coating

被引：0
|
作者：
Samoilenko V.M. [1 ]
Ravilov R.G. [2 ]
Drevnyak V.V. [1 ]
Petrova M.A. [1 ]
机构：
[1] Moscow State Technical University of Civil Aviation, Moscow
[2] Lytkarino Machine-Building Plant, Lytkarino, Moscow obl.
来源：
Samoilenko, V.M. (v-sam61@mail.ru) | 1600年 / Izdatel'stvo Nauka卷 / 2016期
关键词：
Thermal barrier coatings;
D O I：
10.1134/S0036029516060124
中图分类号：
学科分类号：
摘要：
The fracture mechanism of the thermal barrier coating of gas turbine blades is studied. The causes of the fracture of the ceramic layer are discussed and the possible ways to increase the fatigue life of the thermal barrier coating are considered. © 2016, Pleiades Publishing, Ltd.
引用
收藏
页码：555 / 558
页数：3
相关论文
共 50 条
  • [1] Interfacial fracture mechanism associated with mixed oxides growth in thermal barrier coating system
    Xu, Rong
    Fan, Xue Ling
    Zhang, Wei Xu
    Wang, T. J.
    SURFACE & COATINGS TECHNOLOGY, 2014, 253 : 139 - 147
  • [2] Relationship between Interfacial and Coating Fracture Toughnesses of Thermal Barrier Coating
    Tsuge T.
    Waki H.
    Adachi K.
    Hojo T.
    Zairyo/Journal of the Society of Materials Science, Japan, 2020, 69 (12): : 863 - 868
  • [3] Effects of thermal gradient and residual stresses on thermal barrier coating fracture
    Qian, G
    Nakamura, T
    Berndt, CC
    MECHANICS OF MATERIALS, 1998, 27 (02) : 91 - 110
  • [4] FRACTURE ANALYSIS OF THERMAL BARRIER COATING SYSTEMS UNDER THERMAL SHOCK
    Zhang Yan-Yan
    Shen Ri-Lin
    Huang Kai
    Yue Xiao-Ning
    CERAMICS-SILIKATY, 2017, 61 (01) : 59 - 64
  • [5] Fracture analysis of Thermal Barrier Coating Delamination under Thermal Shock
    Chen Ping-wei
    Wang Shao-ming
    Wang Feng-Hui
    2014 ASIA-PACIFIC INTERNATIONAL SYMPOSIUM ON AEROSPACE TECHNOLOGY, APISAT2014, 2015, 99 : 344 - 348
  • [6] Failure Mechanism for Thermal Fatigue of Thermal Barrier Coating Systems
    Giolli, C.
    Scrivani, A.
    Rizzi, G.
    Borgioli, F.
    Bolelli, G.
    Lusvarghi, L.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2009, 18 (02) : 223 - 230
  • [7] Failure Mechanism for Thermal Fatigue of Thermal Barrier Coating Systems
    C. Giolli
    A. Scrivani
    G. Rizzi
    F. Borgioli
    G. Bolelli
    L. Lusvarghi
    Journal of Thermal Spray Technology, 2009, 18 : 223 - 230
  • [8] Instability analysis for thermal barrier coating by fracture mechanical modelings
    Kumar, Amar N.
    Nayak, Amiya
    Patnaik, Alok R.
    Wu, Xijia
    Patnaik, Prakash C.
    PROCEEDINGS OF THE ASME TURBO EXPO 2007, VOL 5, 2007, : 89 - 96
  • [9] Laser Thermal Gradient Testing and Fracture Mechanics Study of a Thermal Barrier Coating
    Yingsang Wu
    Pei-feng Hsu
    Yao Wang
    Mary Helen McCay
    D. Edward Croy
    David Moreno
    Lei He
    Chao Wang
    Hongqi Zhang
    Journal of Thermal Spray Technology, 2019, 28 : 1239 - 1251
  • [10] Laser Thermal Gradient Testing and Fracture Mechanics Study of a Thermal Barrier Coating
    Wu, Yingsang
    Hsu, Pei-feng
    Wang, Yao
    McCay, Mary Helen
    Croy, D. Edward
    Moreno, David
    He, Lei
    Wang, Chao
    Zhang, Hongqi
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2019, 28 (06) : 1239 - 1251
12345