Li2Zn3Ti4O12 Low-Temperature Co-Fired Ceramic with Li2O–B2O3–SiO2 Additive

被引：0
|
作者：
D. I. Vershinin
I. N. Khusainov
N. A. Makarov
机构：
[1] D. I. Mendeleev Russian University of Chemical Technology,
来源：
Glass and Ceramics | 2020年 / 77卷
关键词：
ceramic dielectric; low-temperature co-fired ceramic; LTCC; eutectic additive;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Amaterial for low-temperature co-fired ceramic technology was developed in the Li2O–ZnO–TiO2 system for use in the manufacture of electronic components. The sintering temperature of the material was lowered from 1075 to 950°C by introducing 3% of a sintering additive with a eutectic composition in the Li2O–B2O3–SiO2 system. The developed ceramic obtained at 950°C is characterized by density 4.14 g/cm3 together with the following dielectric properties: permittivity ε = 23.1 and dielectric Q factor Q f = 832 MHz.
引用
收藏
页码：43 / 46
页数：3
相关论文
共 50 条
  • [1] Li2Zn3Ti4O12 Low-Temperature Co-Fired Ceramic with Li2O-B2O3-SiO2 Additive
    Vershinin, D., I
    Khusainov, I. N.
    Makarov, N. A.
    [J]. GLASS AND CERAMICS, 2020, 77 (1-2) : 43 - 46
  • [2] Low-Temperature Co-Firing Ceramic Li2Zn3Ti4O12 Modified by Li2O–ZnO–B2O3 Eutectic Additive
    D. I. Vershinin
    N. A. Makarov
    [J]. Glass and Ceramics, 2018, 75 : 289 - 292
  • [3] Low temperature cofirable Li2Zn3Ti4O12 microwave dielectric ceramic with Li2O–ZnO–B2O3 glass additive
    A. Sayyadi-Shahraki
    E. Taheri-Nassaj
    S. A. Hassanzadeh-Tabrizi
    H. Barzegar-Bafrooei
    [J]. Journal of Materials Science: Materials in Electronics, 2014, 25 : 355 - 360
  • [4] Low-Temperature Co-Firing Ceramic Li2Zn3Ti4O12 Modified by Li2O-ZnO-B2O3 Eutectic Additive
    Vershinin, D. I.
    Makarov, N. A.
    [J]. GLASS AND CERAMICS, 2018, 75 (7-8) : 289 - 292
  • [5] Low temperature cofirable Li2Zn3Ti4O12 microwave dielectric ceramic with Li2O-ZnO-B2O3 glass additive
    Sayyadi-Shahraki, A.
    Taheri-Nassaj, E.
    Hassanzadeh-Tabrizi, S. A.
    Barzegar-Bafrooei, H.
    [J]. JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2014, 25 (01) : 355 - 360
  • [6] Sintering behavior and properties of Li2O–MgO–ZnO–B2O3–SiO2 ceramic composites for applications in low temperature co-fired ceramic (LTCC) technologies
    Fan Yang
    Youhong Tan
    Ye Yuan
    Jin Li
    Caixia Zhang
    Yangfu Liu
    Jianxi Tong
    Fancheng Meng
    [J]. Journal of Materials Science: Materials in Electronics, 2021, 32 : 125 - 132
  • [7] Preparation and properties of low-temperature co-fired ceramic of CaO–SiO2–B2O3 system
    Haikui Zhu
    Min Liu
    Hongqing Zhou
    Liquan Li
    Anguo Lv
    [J]. Journal of Materials Science: Materials in Electronics, 2006, 17 : 637 - 641
  • [8] Fabrication and properties of Li2O–Al2O3–SiO2 glass/Al2O3 composites for low temperature co-fired ceramic applications
    Zhenjun Qing
    Bo Li
    Hao Li
    Yingxiang Li
    Shuren Zhang
    [J]. Journal of Materials Science: Materials in Electronics, 2015, 26 : 1789 - 1794
  • [9] Preparation and Properties of Li2Zn3Ti4O12-Based Ceramics with a Sintering Aid in the Li2O–B2O3–SiO2 System for LTCC Technology
    D. I. Vershinin
    I. N. Khusainov
    N. A. Makarov
    [J]. Inorganic Materials, 2021, 57 : 929 - 936
  • [10] Effect of CaO content on structure and properties of low temperature co-fired glass–ceramic in the Li2O–Al2O3–SiO2 system
    Bo Li
    Zhenjun Qing
    Yingxiang Li
    Hao Li
    Shuren Zhang
    [J]. Journal of Materials Science: Materials in Electronics, 2016, 27 : 2455 - 2459
12345