Low cycle fatigue behaviour of modified and conventional superalloy Inconel 718 at 650°C

被引：0
|
作者：
E. Hari Krishna
Kartik Prasad
Vikas Kumar
Vakil Singh
机构：
[1] Defence Metallurgical Research Laboratory,Department of Metallurgical Engineering
[2] I.T-B.H.U,undefined
来源：
Transactions of the Indian Institute of Metals | 2010年 / 63卷
关键词：
Ni base superalloy; IN 718; low cycle fatigue; cyclic softening; fracture behaviour;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The present investigation deals with the study and comparison of low cycle fatigue (LCF) behavior of modified IN 718 alloy with higher Al+Ti/Nb and Al/Ti ratios of 0.458 and 0.870, with that of conventional IN 718 alloy with corresponding ratios of 0.294 and 0.50 respectively. LCF tests were carried out in total strain control mode at total strain amplitudes (Δɛt/2) from ±0.625% to ±1.0%, in fully reversed loading (R= −1) at 650°C. The modified alloy was found to exhibit better LCF resistance than the conventional alloy.
引用
收藏
页码：63 / 66
页数：3
相关论文
共 50 条
  • [1] Low cycle fatigue behaviour of modified and conventional superalloy Inconel 718 at 650°C
    Krishna, E. Hari
    Prasad, Kartik
    Kumar, Vikas
    Singh, Vakil
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2010, 63 (01): : 63 - 66
  • [2] Fatigue Crack Growth Behaviour of Conventional and Modified IN 718 Superalloys at 650 °C
    E. Hari Krishna
    Kartik Prasad
    Vakil Singh
    Vikas Kumar
    [J]. Transactions of the Indian Institute of Metals, 2013, 66 : 1 - 4
  • [3] Fatigue Crack Growth Behaviour of Conventional and Modified IN 718 Superalloys at 650 A°C
    Krishna, E. Hari
    Prasad, Kartik
    Singh, Vakil
    Kumar, Vikas
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2013, 66 (01) : 1 - 4
  • [4] A comparative evaluation of low cycle fatigue behavior of conventional and modified INCONEL 718
    E. Hari Krishna
    Kartik Prasad
    Vakil Singh
    Vikas Kumar
    [J]. Transactions of the Indian Institute of Metals, 2010, 63 : 515 - 516
  • [5] A comparative evaluation of low cycle fatigue behavior of conventional and modified INCONEL 718
    Krishna, E. Hari
    Prasad, Kartik
    Singh, Vakil
    Kumar, Vikas
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2010, 63 (2-3) : 515 - 516
  • [6] RESIDUAL STRESS FIELD AND LOW-CYCLE FATIGUE BEHAVIOUR OF INCONEL718-PLUS SUPERALLOY
    Dattoma, V.
    De Giorgi, M.
    Nobile, R.
    [J]. ICEM15: 15TH INTERNATIONAL CONFERENCE ON EXPERIMENTAL MECHANICS, 2012,
  • [7] Effect of boron on the low-cycle fatigue behavior and deformation structure of INCONEL 718 at 650 ○C
    Xiao, L
    Chen, DL
    Chaturvedi, MC
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (11): : 3477 - 3487
  • [8] Effect of boron on the low-cycle fatigue behavior and deformation structure of INCONEL 718 at 650 °C
    L. Xiao
    M. C. Chaturvedi
    D. L. Chen
    [J]. Metallurgical and Materials Transactions A, 2004, 35 : 3477 - 3487
  • [9] Low cycle fatigue behavior of Inconel 706 at 650 °C
    Oh, Hojun
    Kim, Soyoung
    Kim, Jung Gi
    Taleghani, Firooz
    Kim, Sangshik
    [J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 17 : 2624 - 2635
  • [10] High-temperature low-cycle fatigue and fatigue-creep behaviour of Inconel 718 superalloy: Damage and deformation mechanisms
    Bartosak, Michal
    Horvath, Jakub
    Galikova, Marketa
    Slany, Michal
    Sulak, Ivo
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2024, 186
12345