Microstructural and mechanical properties of dissimilar friction stir welds between AA6082-T6 and AA7075-T651

In the present work, similar and dissimilar friction stir welds have been produced on 6-mm-thick plates of AA6082-T6 and AA7075-T651. The microstructural characteristics and the mechanical response of both similar and dissimilar welds were investigated aiming to determine the major differences between them. Material mixing of the dissimilar weld nugget, which was created after the welding process, was studied in order to determine the produced different areas and their dominant alloying elements in this zone. Microstructural investigation was made in the welding zones of similar and dissimilar friction stir welds and indications of partial dynamic recrystallization were observed in the thermomechanically affected zone of the similar welds. Transverse and longitudinal microhardness distributions determined the heat affected zone as the weaker area in the welded specimen. After tensile testing, the fracture of the similar and the dissimilar welds at heat affected zone demonstrated the good bonding and weld quality of the similar and dissimilar weld nuggets.