Structural Changes in Binder During Oxidation of Periclase-Carbon Refractories

被引：0
|
作者：
K. I. Ikonnikov
A. A. Kondrukevich
N. S. S’emshchikov
A. V. Belyakov
M. L. Kostochka
机构：
[1] OOO VPO Stal’,
[2] FGBOU VO D. I. Mendeleev Russian Chemical-Technological University,undefined
[3] ANO Chemical Expertise Center,undefined
来源：
Refractories and Industrial Ceramics | 2016年 / 57卷
关键词：
periclase-carbon (PC) objects; carbon-containing components (CC); binder; flaky graphite; periclase; steel-pouring ladle;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Results are given for the change in binder structure in periclase-carbon refractories during heat treatment in an oxidizing atmosphere. After total burn-off at 1000°C carbon, securing periclase grains, the reduction in refractory strength in compression measured at room temperature is 64% of the original, but an object does not disintegrate. An inorganic chemical bond plays the role of a binder consisting of very fine calcium and iron silicates and fine fractions of magnesium, calcium, and iron oxide solid solutions. The results obtained make it possible to predict more reliably the change in refractory properties in service proceeding from the raw material components used.
引用
收藏
页码：384 / 387
页数：3
相关论文
共 50 条
  • [1] Structural Changes in Binder During Oxidation of Periclase-Carbon Refractories
    Ikonnikov, K. I.
    Kondrukevich, A. A.
    S'emshchikov, N. S.
    Belyakov, A. V.
    Kostochka, M. L.
    [J]. REFRACTORIES AND INDUSTRIAL CERAMICS, 2016, 57 (04) : 384 - 387
  • [2] Unfired periclase-carbon refractories on a phenol binder
    Antonov, GI
    [J]. REFRACTORIES AND INDUSTRIAL CERAMICS, 1998, 39 (9-10) : 329 - 333
  • [3] Unfired periclase-carbon refractories on a phenol binder
    G. I. Antonov
    [J]. Refractories and Industrial Ceramics, 1998, 39 : 329 - 333
  • [4] Periclase-carbon composite refractories with a new complex binder
    T. V. Yarushina
    V. A. Akbashev
    V. A. Plyukhin
    A. M. Akbashev
    I. M. Gyrlya
    A. N. Parshikov
    [J]. Refractories and Industrial Ceramics, 2007, 48 : 170 - 175
  • [5] Periclase-carbon composite refractories with a new complex binder
    Yarushina, T. V.
    Akbashev, V. A.
    Plyukhin, V. A.
    Akbashev, A. M.
    Gyrlya, I. M.
    Parshikov, A. N.
    [J]. REFRACTORIES AND INDUSTRIAL CERAMICS, 2007, 48 (03) : 170 - 175
  • [6] Unfired periclase-carbon refractories with a thermoreactive polymer binder
    E. V. Krivokorytov
    N. V. Kononov
    V. S. Osipchik
    B. I. Polyak
    [J]. Refractories and Industrial Ceramics, 1999, 40 : 19 - 24
  • [7] Unfired periclase-carbon refractories with a thermoreactive polymer binder
    Krivokorytov, EV
    Kononov, NV
    Osipchik, VS
    Polyak, BI
    [J]. REFRACTORIES AND INDUSTRIAL CERAMICS, 1999, 40 (1-2) : 19 - 24
  • [8] CARBON AND PERICLASE-CARBON REFRACTORIES
    STARON, J
    [J]. CHEMICKE LISTY, 1992, 86 (08): : 605 - 610
  • [9] Ankersyn - A new generation of periclase-carbon refractories using a carbonaceous binder
    Buchebner, C
    Sampayo, L
    Samm, V
    Blondot, P
    Peruzzi, S
    Boulanger, P
    [J]. REFRACTORIES AND INDUSTRIAL CERAMICS, 2005, 46 (04) : 291 - 294
  • [10] Ankersyn - A new generation of periclase-carbon refractories using a carbonaceous binder
    Buchebner G.
    Sampayo L.
    Samm V.
    Blondot Ph.
    Peruzzi S.
    Boulanger P.
    [J]. Refractories and Industrial Ceramics, 2005, 46 (4) : 291 - 294
12345