Effects of residual stresses on the static and fatigue strength of laser-welded lap joints with different welding speeds

This study was conducted to determine whether the different residual stresses caused by different welding speeds affect the static and fatigue strength of laser-welded lap joints. Residual stresses in STS301L laser-welded lap joints of different thicknesses under two laser-welding speed conditions, 4.1 m/min and 5.1 m/min, were evaluated with the incremental hole-drilling strain gage method at the middle of the heat-affected zone (HAZ). Then, static and fatigue tests were performed. The results show that higher static and fatigue strengths were obtained from the specimens welded with a 4.1 m/min welding speed than from the specimens welded at 5.1 m/min. The main difference was due to the compressive principal residual stress magnitude and its orientation near the HAZ. Also, the micro-hardness profile along the failure interface was measured to verify the static and fatigue failure behavior.