Sustainable soil stabilisation with ground granulated blast-furnace slag activated by olivine and sodium hydroxide

Ground granulated blast-furnace slag (GGBS), activated with olivine (Mg2SiO4) and sodium hydroxide (NaOH), was used to stabilise a clayey soil. Mechanical and microstructural properties of the stabilised soil were assessed through uniaxial compression strength (UCS) tests, X-ray diffraction, scanning electron microscopy and energy-dispersive X-ray spectroscopy (EDS), after curing periods of 7, 18 and 90 days. The UCS of the GGBS-treated soil (without activation with NaOH), even at the highest slag dosage (G(20)S), after 90 days, showed only a slight increase (142 kPa) relatively to the original soil. When olivine was added to the GGBS-treated mixture (O(20)G(20)S), the UCS increased to 444 kPa, after 90 days. However, when NaOH was used as an activator, the UCS of the olivine-GGBS-treated soil (NO(20)G(20)S) increased to more than 6000 kPa, after 90 days. This significant strength increase was attributed to the higher reaction degree provided by the NaOH, which enabled a more effective exploitation (dissolution) of the Ca and Mg present in the slag and olivine, respectively, forming a mixture of C-S-H and M-S-H gels.