Capability of coupled CdSe/TiO2 heterogeneous structure for photocatalytic degradation and photoconductivity

Highly ordered TiO2 nanotube arrays (TiO2-NTAs), with a uniform tube size on titanium substrate, were obtained by means of reoxidation and annealing. A composite structure, CdSe quantum dots@TiO2 nanotube arrays (CdSe QDs@TiO2-NTAs), was fabricated by assembling CdSe quantum dots into TiO2-NTAs via cyclic voltammetry electrochemical deposition. The X-ray diffractometer (XRD), field-emission scanning electron microscope (SEM), and transmission electron microscope (TEM) were carried out for the determination of the composition and structure of the tubular layers. Optical properties were investigated by ultraviolet-visible spectrophotometer (UV-Vis). Photocurrent response under visible light illumination and photocatalytic activity of samples by degradation of methyl orange were measured. The results demonstrated that the photo absorption of the composite film shifted to the visible region, and the photocurrent intensity was greatly enhanced due to the assembly of CdSe QDs. Especially, photocurrent achieved a maximum of 1.853 mu A/cm(2) after five voltammetry cycles of all samples. After irradiation under ultra violet-visible light for 2 h, the degradation rate of composition to methyl orange (MO) reached 88.20%, demonstrating that the CdSe QDs@TiO2-NTAs exhibited higher photocatalytic activity.