Bulk superconducting nano-composites with high critical currents

Flux pinning sites are most effective if their size is comparable to the superconducting coherence length, which is on the nano-meter scale for RE-Ba-Cu-O superconductors [RE = rare earth element]. Introducing nano-phase inclusions directly into the bulk superconducting material has only been partially successful to date, however, due primarily to the absence of chemically stable phases that can co-exist with RE-Ba-Cu-O without suppressing its key superconducting properties. We have identified novel isostructural phases based on (RE) 2Ba4CUMOy (where M = W, Zr, Nb, Ag and Bi) and have fabricated successfully superconducting bulk nano-composites with a high current carrying capability. The average size of the nano-inclusions is observed to vary from 20 nm to 300 nm depending on element M. An observed improvement in Jc under low and high external magnetic fields at 77 K correlates directly with an increased density of nano-inclusions in the superconducting matrix.