Thermal conductivity enhancement of nano-silver particles dispersed ethylene glycol based nanofluids

This contribution reports on the thermal conductivity enhancement of nano-silver particles (nAgPs) based nanofluids with various nAgPs' shapes in view of their potential application in concentrated solar power systems. More accurately, the thermal conductivity behaviour of suspensions of nAgPs dispersed ethylene glycol (nAgPs: EG), prepared by a simple and cost effective chemical synthesis method, is compared with a theoretical prediction. The effect of aging time on the shape of the dispersed nAgPs was clearly observed by the structural, optical and morphological analysis. Spherically shaped and Ag nanowires (AgNWs) with high yields were observed when the nAgPs was aged for 1 and 5 h, respectively. The observed AgNWs showed high aspect ratio (>= 200) when EG and polyvinylpyrrolidone (PVP) were used as reductant and structure-directing agents. The thermal conductivity measurements on nAgPs: EG nanofuids with different volume fractions of nAgPs were conducted in a temperature range 25 < T < 50 degrees C using a guarded hot plate (GHP) method. The thermal conductivity manifested a generally monotonic increase with temperature and an approximately linear relationship with the volume fraction of the nAgPs. Particularly, an enhancement of up to 23% was observed when the nanofluid was aged for 5 h and AgNWs were dominant.