Stress corrosion cracking causes titanium plate heat exchanger failure

被引：0
|
作者：
Turissini, RL [1 ]
Bruno, TV [1 ]
Dahlberg, EP [1 ]
Setterlund, RB [1 ]
机构：
[1] Met Consultants Inc, Houston, TX 77288 USA
来源：
MATERIALS PERFORMANCE | 1998年 / 37卷 / 04期
关键词：
D O I：
暂无
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
引用
收藏
页码：61 / 63
页数：3
相关论文
共 50 条
  • [1] Crevice corrosion under gasket causes titanium plate heat exchanger failure
    Turissini, RL
    Bruno, TV
    Dahlberg, EP
    Setterlund, FB
    [J]. MATERIALS PERFORMANCE, 1998, 37 (01) : 62 - 63
  • [2] Failure avoidance - Stress corrosion cracking of a plate-type heat exchanger
    El-Batahgy, AM
    [J]. MATERIALS PERFORMANCE, 1999, 38 (07) : 60 - 62
  • [3] The corrosion failure analysis of plate pipe for plate heat exchanger
    Song Wen-ming
    Yang Gui-rong
    Hao Yuan
    Zhang Yu-fu
    [J]. ADVANCED ENGINEERING MATERIALS III, PTS 1-3, 2013, 750-752 : 2252 - +
  • [4] Corrosion Failure Analysis of Flow Plate in Plate Heat Exchanger
    Song, Min Ji
    Choi, Gahyun
    Chae, Hobyung
    Kim, Woo Cheol
    Kim, Heesan
    Kim, Jung-Gu
    Lee, Soo Yeol
    [J]. CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2021, 20 (04): : 204 - 209
  • [5] Stress corrosion cracking causes landing gear failure
    不详
    [J]. MATERIALS PERFORMANCE, 2012, 51 (05) : 21 - 22
  • [6] Failure analysis of a titanium plate heat exchanger - Mechanical fatigue
    Pelliccione, A. S.
    SantAnna, R.
    Siqueira, M. H. S.
    Ribeiro, A. F.
    Ramos, J. E.
    Silva, O. P.
    Pimentel, M. F.
    [J]. ENGINEERING FAILURE ANALYSIS, 2019, 105 : 1172 - 1188
  • [7] Failure analysis of stress corrosion cracking in heat exchanger tubes during start-up operation
    Xu, Shugen
    Wang, Chong
    Wang, Weiqiang
    [J]. ENGINEERING FAILURE ANALYSIS, 2015, 51 : 1 - 8
  • [8] STRESS-CORROSION CRACKING AND COMPONENT FAILURE - CAUSES AND PREVENTION
    CHATTERJEE, UK
    [J]. SADHANA-ACADEMY PROCEEDINGS IN ENGINEERING SCIENCES, 1995, 20 : 165 - 184
  • [9] Failure of hydrocracker heat exchanger tubes in an oil refinery by polythionic acid-stress corrosion cracking
    Tawancy, H. M.
    [J]. ENGINEERING FAILURE ANALYSIS, 2009, 16 (07) : 2091 - 2097
  • [10] Stress Corrosion Cracking of Heat Exchanger Tubes in District Heating System
    Cho, Sangwon
    Kim, Seon-Hong
    Kim, Woo-Cheol
    Kim, Jung-Gu
    [J]. CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2019, 18 (02): : 49 - 54
12345