Early stages of subsurface crack and WEC formation in 100Cr6 bearing steel under RCF and hydrogen influence

被引：11

作者：

Lopez-Urunuela, Fernando Jose ^{[1
,2
]}

Fernandez-Diaz, Beatriz ^{[1
]}

Pinedo, Bihotz ^{[1
]}

Aguirrebeitia, Josu ^{[2
]}

机构：

[1] Tekniker, Basque Res & Technol Alliance BRTA, C Inaki Goenaga 5, Eibar 20600, Spain

[2] Univ Basque Country, UPV EHU, Dept Mech Engn, Bilbao, Spain

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2022年 / 155卷

关键词：

White Etching Crack WEC; White Etching Area WEA; Hydrogen embrittlement HE; Rolling Bearing; Rolling Contact Fatigue RCF; WHITE ETCHING CRACKS; ROLLING-CONTACT FATIGUE; NONMETALLIC INCLUSIONS; THRUST BEARING; INITIATION; MATTER; MECHANISM; EVOLUTION; AREAS;

D O I：

10.1016/j.ijfatigue.2021.106587

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Hydrogen precharged specimens were tested in a disc-on-disc tribometer to study the early stages of crack formation that, with cycling, eventually generate WEC or WSF. Specimens whose contact surface was intact were analysed and at subsurface numerous small transgranular cracks were found, as well as sequences of unlinked voids. Premature WEC with fine cracks and little microstructural alteration volume were also found. This paper aims to clarify certain concepts of debate concerning WEC such as the formation of WEAs, the initiation and propagation of cracks and the influence of defects in steel, the mechanisms by which hydrogen favours the development of cracks and WEAs and the transgranular character of cracks. Finally, a crack formation mechanism is proposed which may lead to a novel hypothesis on the mechanism of WEA formation.

引用

页数：18

共 50 条

[1] Influence of Lubricated Rolling/Sliding Tribotesting on Hydrogen Trapping in 100Cr6 Bearing Steel
Weniger, Lisa-Marie
Sefer, Birhan
Pelcastre, Leonardo
Akerfeldt, Pia
Hardell, Jens
[J]. TRIBOLOGY LETTERS, 2024, 72 (03)
[2] Rolling contact fatigue in martensitic 100Cr6: Subsurface hardening and crack formation
Kang, Jee-Hyun
Vegter, R. H.
Rivera-Diaz-del-Castillo, Pedro E. J.
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 607 : 328 - 333
[3] Influence of cryogenic treatment on the wear characteristics of 100Cr6 bearing steel
Siva, R. Sri
Lal, D. Mohan
Nair, P. Kesavan
Jaswin, M. Arockia
[J]. INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2014, 21 (01) : 46 - 51
[4] Influence of cryogenic treatment on the wear characteristics of 100Cr6 bearing steel
R. Sri Siva
D. Mohan Lal
P. Kesavan Nair
M. Arockia Jaswin
[J]. International Journal of Minerals, Metallurgy, and Materials, 2014, 21 : 46 - 51
[5] Influence of cryogenic treatment on the wear characteristics of 100Cr6 bearing steel
R.Sri Siva
D.Mohan Lal
P.Kesavan Nair
M.Arockia Jaswin
[J]. International Journal of Minerals,Metallurgy and Materials, 2014, 21 (01) : 46 - 51
[6] Spheroidization of 100Cr6 Bearing Steel by Warm Forging
M. Vidhyasagar
G. Balachandran
[J]. Transactions of the Indian Institute of Metals, 2021, 74 : 767 - 774
[7] Spheroidization of 100Cr6 Bearing Steel by Warm Forging
Vidhyasagar, M.
Balachandran, G.
[J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2021, 74 (03) : 767 - 774
[8] FE8 type laboratory testing of white etching crack (WEC) bearing failure mode in 100Cr6
Danielsen, H. K.
Guzman, F. Gutierrez
Muskulus, M.
Rasmussen, B. H.
Shirani, M.
Cornel, D.
Sauvage, P.
Wu, J.
Petrov, R.
Jacobs, G.
[J]. WEAR, 2019, 434
[9] INFLUENCE OF MICROSTRUCTURE ON CRACK INITIATION AND PROPAGATION ON TITANIUM-ALLOYS AND STEEL (100CR6)
BOHM, W
[J]. ZEITSCHRIFT FUR METALLKUNDE, 1981, 72 (10): : 693 - 699
[10] Study of BN formation by dual implantation of boron and nitrogen in a 100Cr6 bearing steel
Faussemagne, A.
Delichere, P.
Moncoffre, N.
Benyagoub, A.
Marest, G.
[J]. 1996, Elsevier Science S.A., Lausanne, Switzerland (83)

← 1 2 3 4 5 →