Steam oxidation resistance of Ni-Cr thermal spray coatings on 9Cr-1Mo steel. Part 1: 80Ni-20Cr

被引：66

作者：

Sundararajan, T ^{[1
]}

Kuroda, S ^{[1
]}

Itagaki, T ^{[1
]}

Abe, F ^{[1
]}

机构：

[1] Natl Inst Mat Sci, Tsukuba, Ibaraki 3050047, Japan

来源：

ISIJ INTERNATIONAL | 2003年 / 43卷 / 01期

关键词：

steam oxidation; Cr-Mo steel; Ni-Cr coating; high velocity oxy fuel spray and atmospheric plasma spray;

D O I：

10.2355/isijinternational.43.95

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The steam oxidation resistance of 80%Ni-20%Cr metallic coatings has been evaluated at four different steam temperatures in the range of 600-750degreesC. Substrate used for the study was 9Cr-1Mo type steel. The thermal spray coatings were carried out using two different processes, viz., atmospheric plasma spray (APS) and high velocity oxy fuel (HVOF) spray. Thickness of the coatings was about 40 and 60,mum respectively. The results show that the thick and dense HVOF coating showed a better steam oxidation resistance than the thin porous APS coatings. At prolonged aging (1000 h) the HVOF coating showed the best protection till the temperature range of 650degreesC. Beyond this temperature the presence of Fe2O3 was noticed at the coating surface. The reason for the protectiveness and failure at higher temperatures (above 650degreesC) are discussed in detail.

引用

页码：95 / 103

页数：9

共 50 条

[1] Steam oxidation resistance of Ni-Cr thermal spray coatings on 9Cr-1Mo steel. Part 2: 50Ni-50Cr
Sundararajan, T
Kuroda, S
Itagaki, T
Abe, F
ISIJ INTERNATIONAL, 2003, 43 (01) : 104 - 111
[2] Steam oxidation of 80Ni-20Cr high-velocity oxyfuel coatings on 9Cr-1Mo steel: Diffusion-induced phase transformations in the substrate adjacent to the coating
T. Sundararajan
S. Kuroda
F. Abe
Metallurgical and Materials Transactions A, 2005, 36 : 2165 - 2174
[3] Effect of thermal spray on the microstructure and adhesive strength of high-velocity oxy-fuel-sprayed Ni-Cr coatings on 9Cr-1Mo steel
T. Sundararajan
S. Kuroda
F. Abe
Metallurgical and Materials Transactions A, 2004, 35 : 3187 - 3199
[4] Effect of thermal spray on the microstructure and adhesive strength of high-velocity oxy-fuel-sprayed Ni-Cr coatings on 9Cr-1Mo steel
Sundararajan, T
Kuroda, S
Abe, F
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (10): : 3187 - 3199
[5] Steam oxidation of 80Ni-20Cr high-velocity oxyfuel coatings on 9Cr-1 Mo steel: Diffusion-induced phase transformations in the substrate adjacent to the coating
Sundararajan, T
Kuroda, S
Abe, F
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2005, 36A (08): : 2165 - 2174
[6] Behaviour of Mn and Si in the spray powders during steam oxidation of Ni-Cr thermal spray coatings
Sundararajan, T
Kuroda, S
Nishida, K
Itagaki, T
Abe, F
ISIJ INTERNATIONAL, 2004, 44 (01) : 139 - 144
[7] SODIUM COMPATIBILITY OF 9Cr-1Mo FERRITIC STEEL.
Hooper, A.J.
Proceedings of the Annual Reliability and Maintainability Symposium, 1980, 1 : 35 - 7
[8] Steam oxidation studies on 50Ni-50Cr HVOF coatings on 9Cr-1Mo steel: Change in structure and morphology across the coating/substrate interface
Sundararajan, T
Kuroda, S
Abe, F
MATERIALS TRANSACTIONS, 2004, 45 (04) : 1299 - 1305
[9] OXIDATION OF 80NI-20CR ALLOYS IN CARBON MONOXIDE AT HIGH TEMPERATURES
OSTHAGEN, K
CORROSION, 1964, 20 (08) : T252 - &
[10] Effect coating thickness and the sealant on the steam oxidation resistance of APS Ni-Cr coatings
Sundararajan, T
Haruyama, H
Kuroda, S
Abe, F
Thermal Spray 2004: Advances in Technology and Application, Proceedings, 2004, : 442 - 447

← 1 2 3 4 5 →