Gas-Sensing Properties of Nano-LaFeO3 Prepared by a Simple Molten-Salt Method

被引：0
|
作者：
Jiang Dongli [1 ]
Chu Xiangfeng [2 ]
机构：
[1] Guilin Med Univ, Coll Pharm, Guilin 541004, Peoples R China
[2] Sun Yat Sen Univ, Guangzhou 510275, Guangdong, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2009年 / 38卷 / 10期
关键词：
LaFeO3; molten-salt method; triethylamine; gas-sensing properties; LAFEO3; FILM; SENSORS; POWDERS;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Nanocrystalline LaFeO3 was prepared by a simple molten-salt method with La2O3 and FeCl3 center dot 6H(2)O as main starting materials. The nanocrystalline samples were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM) for the phases and morphology. Their gas-sensing properties to triethylamine, C2H5OH, gasoline, C6H6 and CH3COCH3 were investigated. The results demonstrated that pure LaFeO3 nanocrystalline with uniform grain sizes and an average diameter of about 40 nm was formed when calcined at 800 degrees C. Moreover, the gas sensor made of the nanocrystalline LaFeO3 sample showed high sensitivity as well as good selectivity to dilute triethylamine. The LaFeO3 sensor showed the sensitivity as high as 7.9 to even 25 mu g/g triethylamine at 250 degrees C, and the response and recovery time are 6 and 13 s, respectively.
引用
收藏
页码：1848 / 1851
页数：4
相关论文
共 11 条
  • [1] Microstructural evolution of nanosized LaFeO3 powders from the thermal decomposition of a cyano-complex for thick film gas sensors
    Carotta, MC
    Butturi, MA
    Martinelli, G
    Sadaoka, Y
    Nunziante, P
    Traversa, E
    [J]. SENSORS AND ACTUATORS B-CHEMICAL, 1997, 44 (1-3) : 590 - 594
  • [2] CH3SH-sensing characteristics of LaFeO3 thick-film prepared by co-precipitation method
    Chu, XF
    Siciliano, P
    [J]. SENSORS AND ACTUATORS B-CHEMICAL, 2003, 94 (02) : 197 - 200
  • [3] Preparation and acetone sensitive characteristics of nano-LaFeO3 semiconductor thin films by polymerization complex method
    Liu, Xiaochuan
    Ji, Huiming
    Gu, Yanfei
    Xu, Mingxia
    [J]. MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2006, 133 (1-3): : 98 - 101
  • [4] Large-scale synthesis of single-crystal line perovskite nanostructures
    Mao, YB
    Banerjee, S
    Wong, SS
    [J]. JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2003, 125 (51) : 15718 - 15719
  • [5] Niu XS, 2005, RARE METAL MAT ENG, V34, P124
  • [6] Nanocrystalline orthoferrite powders: Synthesis and magnetic properties
    Rajendran, M.
    Bhattacharya, A. K.
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2006, 26 (16) : 3675 - 3679
  • [7] Gas sensing with semiconducting perovskite oxide LaFeO3
    Toan, NN
    Saukko, S
    Lantto, V
    [J]. PHYSICA B-CONDENSED MATTER, 2003, 327 (2-4) : 279 - 282
  • [8] Environmental monitoring field tests using screen-printed thick-film sensors based on semiconducting oxides
    Traversa, E
    Sadaoka, Y
    Carotta, MC
    Martinelli, G
    [J]. SENSORS AND ACTUATORS B-CHEMICAL, 2000, 65 (1-3) : 181 - 185
  • [9] WANG J, 1997, J FUNCTIONAL MAT, V28, P165
  • [10] A high performance ethanol sensor based on field-effect transistor using a LaFeO3 nano-crystalline thin-film as a gate electrode
    Zhao, SQ
    Sin, JKO
    Xu, BK
    Zhao, MY
    Peng, ZY
    Cai, H
    [J]. SENSORS AND ACTUATORS B-CHEMICAL, 2000, 64 (1-3) : 83 - 87
12