Bioactivity of self-organized TiO2 nanotubes used as surface treatment on Ti biomaterials

Titanium and its alloys are widely used as implants due to their excellent mechanical properties, corrosion resistance and biocompatibility. TiO2 nanotubes have been studied as surface treatment to increase the specific area and to improve osseointegration. However, the thermodynamic stability and bioactivity of these nanostructures must be evaluated. The objective of this research was to obtain nanotubes oxides on Ti6Al4V alloy and to analyze the electrochemical stability in physiological solution at 37 degrees C and the bioactive response of the biomaterial. The nanotubes were obtained by potentiostatic anodization. The morphology of the oxides was evaluated by scanning electron microscopy. The chemical characterization was analyzed by energy dispersive spectroscopy and x-ray photoelectron spectroscopy techniques. The electrochemical stability was analyzed by open circuit potential (OCP) and the bioactivity by biomimetic test in a simulated body fluid (SBF) solution. The OCP of the nanotubes oxides was shown to be more noble and stable than the compacted oxides. The biomaterial covered with theses oxides showed sealing by Ca and P after 30 d immersion in artificial blood. And after 15 d of immersion in SBF, the hydroxyapatite could be seen on the non-sealed nanotubes. TiO2 nanotube layers could improve the superficial chemical stability and also the osseointegration process.