Effect of temperature on hot corrosion of nickel-based alloys for 700? A-USC power plants

被引：14

作者：

Pan, Peiyuan ^{[1
]}

Li, Tongyu ^{[1
]}

Wang, Yuzhou ^{[1
]}

Zhang, Naiqiang ^{[1
]}

Chen, Heng ^{[1
]}

机构：

[1] North China Elect Power Univ, Key Lab Condit Monitoring & Control Power Plant Eq, Minist Educ, Beijing 102206, Peoples R China

来源：

CORROSION SCIENCE | 2022年 / 203卷

基金：

中国博士后科学基金;

关键词：

Superalloys; Molten salts; SEM; Weight loss; Hot corrosion; Sulphidation; METAL-SULFUR SYSTEMS; NI-BASED ALLOYS; PHASE-RELATIONSHIPS; FIRESIDE CORROSION; COAL; ASH; OXIDATION; ALUMINUM; BEHAVIOR; THERMODYNAMICS;

D O I：

10.1016/j.corsci.2022.110350

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Nickel-based alloys were exposed to a synthetic flue gas at varying temperatures from 700 ? to 800 ?. Two main damage mechanisms were revealed, including general surface oxidation caused by eutectic melting of sulfates and internal cracking caused by sulfur diffusion. The damage level of the alloys did not monotonically increase with temperature. Significant weight losses due to molten sulfate corrosion were found at 700-760 ?, and the minimum damage was at 780 ?. Nimonic 263 with the highest cobalt, titanium contents and the lowest aluminum content exhibited the best resistance to both molten sulfate corrosion and sulfur invasion.

引用

页数：18

共 50 条

[1] Hot deformation characteristics and processing map analysis of a new designed nickel-based alloy for 700 °C A-USC power plant
Wu, Yunsheng
Zhang, Maicang
Xie, Xishan
Dong, Jianxin
Lin, Fusheng
Zhao, Shuangqun
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 656 : 119 - 131
[2] Heat Treatment of a Candidate Material for 700 ℃ A-USC Power Plants
Yan CHONG
Zheng-dong LIU
Andy GODFREY
Lu WANG
Wei LIU
Yu-qing WENG
[J]. Journal of Iron and Steel Research(International), 2015, 22 (02) : 150 - 156
[3] Heat Treatment of a Candidate Material for 700 °C A-USC Power Plants
Yan Chong
Zheng-dong Liu
Andy Godfrey
Lu Wang
Wei Liu
Yu-qing Weng
[J]. Journal of Iron and Steel Research International, 2015, 22 : 150 - 156
[4] Heat Treatment of a Candidate Material for 700 °C A-USC Power Plants
Chong, Yan
Liu, Zheng-dong
Godfrey, Andy
Wang, Lu
Liu, Wei
Weng, Yu-qing
[J]. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2015, 22 (02) : 150 - 156
[5] Behaviour of Alloy 617 OCC Under Hot Corrosion Conditions Encountered in Boilers in A-USC Power Plants
P. R. Hari
N. Arivazhagan
M. Nageswara Rao
A. H. V. Pavan
[J]. Transactions of the Indian Institute of Metals, 2019, 72 : 1511 - 1514
[6] Behaviour of Alloy 617 OCC Under Hot Corrosion Conditions Encountered in Boilers in A-USC Power Plants
Hari, P. R.
Arivazhagan, N.
Rao, M. Nageswara
Pavan, A. H. V.
[J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2019, 72 (06) : 1511 - 1514
[7] HOT CORROSION STUDIES ON NICKEL-BASED ALLOYS CONTAINING SILICON
KERR, TW
SIMKOVICH, G
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1976, 123 (08) : C252 - C252
[8] OXIDATION AND HOT CORROSION OF NICKEL-BASED ALLOYS CONTAINING MOLYBDENUM
PETERS, KR
WHITTLE, DP
STRINGER, J
[J]. CORROSION SCIENCE, 1976, 16 (11) : 791 - &
[9] Dynamic recrystallization of a new nickel-based alloy for 700 °C A-USC power plant applications with different initial states: as-homogenized and as-forged
Wu, Yunsheng
Zhang, Maicang
Xie, Xishan
Lin, Fusheng
Zhao, Shuangqun
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 662 : 283 - 295
[10] Effect of Creep Degradation on Hardness Changes of Ni-based Alloys for A-USC Power Boiler
Saito, Nobuhiko
Ishiyama, Kazuki
Yamaguchi, Tomiko
Masuyama, Fujimitsu
[J]. ISIJ INTERNATIONAL, 2019, 59 (09) : 1695 - 1704

← 1 2 3 4 5 →