Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I-effect of heat control on welding stresses and stress relief cracking (vol 64, pg 807, 2020)

被引：0
|
作者：
Kromm, A. [1 ]
Lausch, T. [1 ]
Schroepfer, D. [1 ]
Rhode, M. [1 ,2 ]
Kannengiesser, T. [1 ,2 ]
机构：
[1] Bundesanstalt Mat Forsch & Prufung BAM, Berlin, Germany
[2] Otto von Guericke Univ, Inst Mat Sci & Joining Technol, Magdeburg, Germany
来源：
WELDING IN THE WORLD | 2021年 / 65卷 / 11期
关键词：
D O I：
10.1007/s40194-021-01166-4
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
引用
收藏
页码：2249 / 2249
页数：1
相关论文
共 10 条
  • [1] Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I-effect of heat control on welding stresses and stress relief cracking
    Kromm, A.
    Lausch, T.
    Schroepfer, D.
    Rhode, M.
    Kannengiesser, T.
    WELDING IN THE WORLD, 2020, 64 (05) : 807 - 817
  • [2] Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I—effect of heat control on welding stresses and stress relief cracking
    A. Kromm
    T. Lausch
    D. Schroepfer
    M. Rhode
    T. Kannengiesser
    Welding in the World, 2020, 64 : 807 - 817
  • [3] Correction to: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I—effect of heat control on welding stresses and stress relief cracking
    A. Kromm
    T. Lausch
    D. Schroepfer
    M. Rhode
    T. Kannengiesser
    Welding in the World, 2021, 65 : 2249 - 2249
  • [4] Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment (vol 64, pg 819, 2020)
    Kromm, A.
    Lausch, T.
    Schroepfer, D.
    Rhode, M.
    Kannengiesser, T.
    WELDING IN THE WORLD, 2021, 65 (11) : 2251 - 2251
  • [5] Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment
    Kromm, A.
    Lausch, T.
    Schroepfer, D.
    Rhode, M.
    Kannengiesser, T.
    WELDING IN THE WORLD, 2020, 64 (05) : 819 - 829
  • [6] Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment
    A. Kromm
    T. Lausch
    D. Schroepfer
    M. Rhode
    T. Kannengiesser
    Welding in the World, 2020, 64 : 819 - 829
  • [7] Correction to: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment
    A. Kromm
    T. Lausch
    D. Schroepfer
    M. Rhode
    T. Kannengiesser
    Welding in the World, 2021, 65 : 2251 - 2251
  • [8] Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part III: assessment of residual stresses from small-scale to real component welds
    D. Schroepfer
    A. Kromm
    T. Lausch
    M. Rhode
    R. C. Wimpory
    T. Kannengiesser
    Welding in the World, 2021, 65 : 1671 - 1685
  • [9] Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part III: assessment of residual stresses from small-scale to real component welds
    Schroepfer, D.
    Kromm, A.
    Lausch, T.
    Rhode, M.
    Wimpory, R. C.
    Kannengiesser, T.
    WELDING IN THE WORLD, 2021, 65 (09) : 1671 - 1685
  • [10] A Study on Microstructure, Residual Stresses and Stress Corrosion Cracking of Repair Welding on 304 Stainless Steel: Part I-Effects of Heat Input
    Luo, Yun
    Gu, Wenbin
    Peng, Wei
    Jin, Qiang
    Qin, Qingliang
    Yi, Chunmei
    MATERIALS, 2020, 13 (10)
1