A comparison of short and long fatigue crack growth in steel

被引：22
|
作者：
Kaynak, C [1 ]
Ankara, A [1 ]
Baker, TJ [1 ]
机构：
[1] UNIV LONDON IMPERIAL COLL SCI TECHNOL & MED, DEPT MAT, LONDON, ENGLAND
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 1996年 / 18卷 / 01期
关键词：
short cracks; long cracks;
D O I：
10.1016/0142-1123(95)00074-7
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
In this study, the growth behaviour of short fatigue cracks in En7A steel with a high content of elongated MnS inclusions has been investigated by generating and evaluating short crack growth data for the six principal specimen orientations. The anomalous initiation and growth behaviour of short cracks was also compared with that of long crack data for the same material and loading conditions determined before. This comparison revealed the sub-threshold initiation and faster growth rate of short cracks compared with long cracks under the same stress intensity factor range. In order to simulate this discrepancy between short and long cracks, a crack closure model for long crack data was used.
引用
收藏
页码：17 / 23
页数：7
相关论文
共 50 条
  • [1] CRACK CLOSURE AND THE GROWTH OF SHORT AND LONG FATIGUE CRACKS
    MCEVILY, AJ
    MINAKAWA, K
    [J]. SCRIPTA METALLURGICA, 1984, 18 (01): : 71 - 76
  • [2] Inclusion induced anisotropy of short fatigue crack growth in steel
    Kaynak, C
    Ankara, A
    Baker, TJ
    [J]. MATERIALS SCIENCE AND TECHNOLOGY, 1996, 12 (07) : 557 - 562
  • [3] Both short and long fatigue crack growth in an austenitic stainless steel at 650 degrees C
    Polvora, JP
    Drubay, YB
    Piques, R
    Martelet, YB
    [J]. ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 1255 - 1260
  • [4] Fatigue cracks in Eurofer 97 steel: Part II. Comparison of small and long fatigue crack growth
    Kruml, T.
    Hutar, P.
    Nahlik, L.
    Seitl, S.
    Polak, J.
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2011, 412 (01) : 7 - 12
  • [5] SHORT AND LONG FATIGUE CRACK-GROWTH - A UNIFIED MODEL
    NAVARRO, A
    DELOSRIOS, ER
    [J]. PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1988, 57 (01): : 15 - 36
  • [6] CRACK DEFLECTION - IMPLICATIONS FOR THE GROWTH OF LONG AND SHORT FATIGUE CRACKS
    SURESH, S
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1983, 14 (11): : 2375 - 2385
  • [7] COMPARISON OF SHORT AND LONG FATIGUE CRACK-GROWTH IN 7075-T6 ALUMINUM
    BU, R
    STEPHENS, RI
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1986, 9 (01) : 35 - 48
  • [8] Influence of texture on the short fatigue crack growth in austenitic stainless steel
    Mikulich, V.
    Blochwitz, C.
    Skrotzki, W.
    Tirschler, W.
    [J]. MATERIALS SCIENCE, 2006, 42 (04) : 514 - 526
  • [9] Corrosion fatigue short crack growth behaviour in a high strength steel
    Murtaza, G
    Akid, R
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 1996, 18 (08) : 557 - 566
  • [10] Short fatigue crack growth behaviour of a ferritic steel weld metal
    Venkateswaran, P
    Raman, SGS
    Pathak, SD
    [J]. SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2005, 10 (01) : 95 - 102
12345