Vacuum diffusion bonding of TiB2 cermet to TiAl based alloys

被引：9
|
作者：
Li, ZR [1 ]
Feng, JC [1 ]
Cao, J [1 ]
机构：
[1] Harbin Inst Technol, State Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2004年 / 20卷 / 12期
关键词：
titanium boride ceramic; titanium aluminide; diffusion bonding;
D O I：
10.1179/026708304225016798
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Vacuum diffusion bonding of TiB2 cermet to TiAl based alloys was carried out at 1123-1323 K for 0.6-3.6 ks under 80 MPa. The microstructural analyses indicate that a compound Ti(Cu,Al)(2) is formed in the interface of the TiB2/TiAl joints, and the width and quantity of the Ti(Cu,Al)(2) compound increase with the increase of the bonding temperature and bonding time. The experimental results show that the shear strength of the diffusion bonded TiB2/TiAl joint is 103 MPa, when TiB2 cermet is bonded to TiAl based alloy at 1223 K for 1.8 ks under 80 MPa.
引用
收藏
页码：1666 / 1668
页数：3
相关论文
共 50 条
  • [1] Microstructure and strength of brazed joints of TiB2 cermet to TiAl-based alloys
    李卓然
    冯吉才
    曹健
    China Welding, 2003, (01) : 19 - 21
  • [2] Vacuum brazing of TiB2 cermet to TiAl-based alloys using Ag-Cu-Zn filler metal
    Li, ZR
    Feng, JC
    Cao, J
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2003, 13 : 39 - 41
  • [3] Microstructure and strength of the TiB2 cermet/TiAl joint diffusion bonded with Ni interlayer
    Li, ZR
    Feng, JC
    Cao, J
    Qian, YY
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2003, 19 : 181 - 183
  • [4] FEM analysis of thermal/residual stresses in brazing TiB2 cermet/TiAl joints
    Li, Zhuo-Ran
    Cao, Jian
    Feng, Ji-Cai
    Hanjie Xuebao/Transactions of the China Welding Institution, 2003, 24 (03): : 1 - 4
  • [5] Grain refinement of TiAl-based alloys: The role of TiB2 crystallography and growth
    Gosslar, D.
    Guenther, R.
    Hecht, U.
    Hartig, C.
    Bormann, R.
    ACTA MATERIALIA, 2010, 58 (20) : 6744 - 6751
  • [6] Effect of TiB2 on microstructure, mechanical properties and oxidation resistance of TiAl-based alloys
    Xiao, Shu-Long (xiaoshulong@hit.edu.cn), 1600, Central South University of Technology (26):
  • [7] Diffusion bonding between TiAl based alloys and steels
    Han, W.B.
    Zhang, J.H.
    Journal of Materials Science and Technology, 2001, 17 (01): : 191 - 192
  • [8] Diffusion Bonding between TiAl Based Alloys and Steels
    Wenbo HAN and Jiuhai ZHANG National Key Laboratory of Precision Hot Processing of Metals
    Journal of Materials Science & Technology, 2001, (01) : 191 - 192
  • [9] Diffusion bonding between TiAl based alloys and steels
    Han, WB
    Zhang, JH
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2001, 17 (01) : 191 - 192
  • [10] Microstructure and mechanical properties of TiB2/FeMo Cermet
    Miao, MQ
    Fu, ZY
    Zhang, JY
    Gong, LJ
    JOURNAL OF INORGANIC MATERIALS, 2005, 20 (02) : 499 - 502
12345