Fabrication and properties of porous alumina ceramics with three different pore sizes

被引：16
|
作者：
Dong, Binbin [1 ]
Wang, Gang [1 ]
Yuan, Bo [1 ]
Han, Jianshen [1 ]
Chen, Kuo [1 ]
Li, Hongxia [1 ]
机构：
[1] Sinosteel Luoyang Inst Refractories Res Co Ltd, State Key Lab Adv Refractories, Luoyang 471039, Peoples R China
来源：
JOURNAL OF POROUS MATERIALS | 2017年 / 24卷 / 03期
基金：
中国国家自然科学基金;
关键词：
Porous alumina ceramics; Drying methods; Pore size; Suspension emulsion; Direct foaming; Solid template; THERMAL-CONDUCTIVITY; MICROSTRUCTURE; STRENGTH; POROSITY;
D O I：
10.1007/s10934-016-0319-4
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Porous alumina ceramics with uniform total porosity (69.6-70.3%), spherical pores, and different pore size (22.9 +/- 10.3, 197.7 +/- 80.0 and 714.1 +/- 207.2 mu m) were prepared by using suspension emulsion, direct foaming, and solid template as pore forming mechanism, respectively and gelcasting technology. Different drying methods were selected according to the different pore forming agents. Pore size could significantly affect the mechanical and thermal properties. The compressive strength decreased evidently from 116.25 +/- 10.96 to 22.43 +/- 1.15 MPa and thermal conductivity of 1000 A degrees C increased from 0.28 +/- 0.01 to 0.58 +/- 0.01 W/(m K) with the increasing pore size (from 22.9 +/- 10.3 to 714.1 +/- 207.2 mu m).
引用
收藏
页码：805 / 811
页数：7
相关论文
共 50 条
  • [1] Fabrication and properties of porous alumina ceramics with three different pore sizes
    Binbin Dong
    Gang Wang
    Bo Yuan
    Jianshen Han
    Kuo Chen
    Hongxia Li
    [J]. Journal of Porous Materials, 2017, 24 : 805 - 811
  • [2] Preparation and characterization of porous alumina ceramics using different pore agents
    Ali, Mohammed Sabah
    Hanim, M. A. Azmah
    Tahir, S. M.
    Jaafar, C. N. A.
    Norkhairunnisa, M.
    Matori, Khamirul Amin
    [J]. JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2017, 125 (05) : 402 - 412
  • [3] The fabrication of porous mullite ceramics based on the different sizes of aluminum hydroxide
    Shan, Qingliang
    Ma, Qian
    Lian, Jiawei
    Yao, Caiyu
    Shui, Anze
    [J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2022, 19 (05) : 2675 - 2685
  • [4] Effect of Different Particle Sizes and Pore-Making Agent Ratio on Properties of SiC Porous Ceramics
    Li, Huan
    Xu, Chengshi
    Chen, Juntai
    Ma, Mengen
    Deng, Xiangyun
    [J]. 6TH ANNUAL INTERNATIONAL WORKSHOP ON MATERIALS SCIENCE AND ENGINEERING, 2020, 1622
  • [5] Fabrication and properties of porous anorthite ceramics with modelling pore structure
    Li, Cuiwei
    Han, Yao
    Wu, Linghao
    Chen, Kepi
    An, Li-nan
    [J]. MATERIALS LETTERS, 2017, 190 : 95 - 98
  • [6] Fabrication of bimodal porous alumina ceramics
    Han, YS
    Li, JB
    Chen, YJ
    [J]. MATERIALS RESEARCH BULLETIN, 2003, 38 (02) : 373 - 379
  • [7] Effect of alumina fiber content on pore structure and properties of porous ceramics
    Lang, Ying
    Zhao, Lin
    Dai, Xin
    Wang, Chang-An
    [J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2019, 16 (02) : 814 - 819
  • [8] Fabrication of porous alumina ceramics by starch consolidation
    Qi Jianqiang
    Huang Yong
    Ouyang Shixi
    Chen Ruifeng
    [J]. RARE METAL MATERIALS AND ENGINEERING, 2007, 36 : 337 - 340
  • [9] Research on CMP performances of flower-like porous alumina abrasives with different pore sizes
    [J]. Bu, N. (bunaijing@163.com), 1600, Inderscience Enterprises Ltd. (05):
  • [10] Porous Alumina Ceramics with Multimodal Pore Size Distributions
    Biggemann, Jonas
    Stumpf, Martin
    Fey, Tobias
    [J]. MATERIALS, 2021, 14 (12)
12345