Investigation of High Temperature Corrosion Behavior on 304L Austenite Stainless Steel in Corrosive Environments

In this work, 304L stainless steel samples were exposed at 700 degrees C for 10hrs in different corrosive environments; dry oxygen, molten salt, and molten salt + dry oxygen. The corrosion behavior of samples was analyzed using weight change measurement technique, optical microscope (OM) and Scanning Electron Microscope (SEM) equipped with Energy Dispersive X-ray (EDX). The existence phases of corroded sample were determined using X-ray Diffraction (XRD). The lowest corrosion rate was recorded in dry oxygen while the highest was in molten salt + dry oxygen environments with the value of 0.0062 mg/cm(2) and -13.5225 mg/cm(2) respectively. The surface morphology of sample in presence of salt mixture showed scale spallation. Oxide scales of Fe3O4, Fe2O3 were the main phases developed and detected by XRD technique. Cr2O3 was not developed in every sample as protective layers but chromate-rich oxide was developed. The cross-section analysis found the oxide scales were in porous, thick and non-adherent that would not an effective barrier to prevent from further degradation of alloy. EDX analysis also showed the Cr-element was low compared to Fe-element at the oxide scale region.