Evolution of structure during the oxidation of zirconium diboride-silicon carbide in air up to 1500°C

The structures that developed as dense ZrB2-SiC ceramics were heated to 1500 degrees C in air were characterized using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction. The oxidation behavior was also studied using thermal gravimetric analysis (TGA). Below 1200 degrees C, a protective B2O3-rich scale was observed on the surface. At 1200 degrees C and above, the B2O3 evaporated and the SiO2-rich scale that formed was stable up to at least 1500 degrees C. Beneath the surface, layers that were rich in zirconium oxide, and from which the silicon carbide had been partially depleted. were observed. The observations were consistent with the oxidation sequence recorded by thermal gravimetric analysis. (c) 2006 Elsevier Ltd. All rights reserved.