Effect of silicon on microstructure and stress rupture properties of a corrosion resistant Ni-based superalloy during long term thermal exposure

被引：25
|
作者：
Liu, T. [1 ,2 ]
Dong, J. S. [2 ]
Xie, G. [2 ,3 ]
Wang, L. [2 ,3 ]
Lou, L. H. [2 ]
机构：
[1] Jiangsu Univ Technol, Sch Mat Sci & Engn, Changzhou 213001, Peoples R China
[2] Chinese Acad Sci, Inst Met Res, Superalloys Div, Shenyang 110016, Peoples R China
[3] Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2016年 / 656卷
基金：
中国国家自然科学基金;
关键词：
Corrosion resistant superalloy; Thermal exposure; Microstructure; Stress rupture properties; Silicon; CREEP-PROPERTIES; PRECIPITATION; NICKEL; ALLOY; CARBIDES; CEMENTITE; EVOLUTION; STEELS;
D O I：
10.1016/j.msea.2015.11.018
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The influence of silicon on microstructure and stress rupture properties of GH3535 nickel-based superalloy during long term thermal exposure at 700 degrees C was investigated. After long term thermal exposure, the secondary carbides precipitated along grain boundaries. Si addition induced the formation of M12C carbides, while only M6C carbides were observed in Si free alloy. The secondary M12C carbides exhibited particular orientation relationship with matrix for the alloy with Si, but the secondary M6C carbides are incoherent with matrix for the Si free alloy. It is believed that the difference in the types of the secondary carbides was originated from Si. The stress rupture life decreased after 1000 h thermal exposure for the Si free alloy, but no noticeable changes could be detected for the alloy with Si. The interface between the secondary M6C carbides and matrix became the main site for crack initiation after 1000 h thermal exposure for the Si free alloy. But no cracks was detected at the interface between the secondary M12C carbides and matrix even after 10,000 h thermal exposure, which may be related to the strong interfacial cohesive force between secondary carbides and matrix. (C) 2016 Published by Elsevier B.V.
引用
收藏
页码：75 / 83
页数：9
相关论文
共 50 条
  • [1] The Effect of Long-Term Thermal Exposure on the Microstructure and Stress Rupture Property of a Directionally Solidified Ni-Based Superalloy
    Jiang, X. W.
    Wang, D.
    Xie, G.
    Li, H.
    Lou, L. H.
    Zhang, J.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (13): : 6016 - 6026
  • [2] The Effect of Long-Term Thermal Exposure on the Microstructure and Stress Rupture Property of a Directionally Solidified Ni-Based Superalloy
    X. W. Jiang
    D. Wang
    G. Xie
    H. Li
    L. H. Lou
    J. Zhang
    Metallurgical and Materials Transactions A, 2014, 45 : 6016 - 6026
  • [3] The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure
    Wang, Jian
    Zhou, Lanzhang
    Sheng, Liyuan
    Guo, Jianting
    MATERIALS & DESIGN, 2012, 39 : 55 - 62
  • [4] Effects of Cr content on the microstructure and stress rupture property of a directionally solidified Ni-based superalloy during long-term thermal exposure
    Zhang, H. W.
    Qin, X. Z.
    Wu, Y. S.
    Zhou, L. Z.
    Li, X. W.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 718 : 449 - 460
  • [5] Effect of Long-Term Aging on Microstructure Evolution and Stress Rupture Properties of Ni-Based Single Crystal Superalloy
    Wen Tao
    Li Jinguo
    Liu Lirong
    Chen Lijia
    Jin Tao
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 (02) : 230 - 234
  • [6] Microstructural evolution and stress rupture behaviour of a Ni-Based wrought superalloy during thermal exposure
    Kong, Weiwen
    Wang, Yongqiang
    Yuan, Chao
    Zhang, Baoning
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 822
  • [7] Effect of Ta on the Microstructure and Creep Properties of a Hot-Corrosion Resistant Ni-Based Single-Crystal Superalloy After Long-Term Exposure
    Liu Jing
    Zhang Siqian
    Wang Dong
    Wang Li
    Chen Lijia
    ACTA METALLURGICA SINICA, 2024, 60 (02) : 179 - 188
  • [8] Effect of Long-term Thermal Exposure on Microstructure and Stress Rupture Properties of GH3535 Superalloy
    T.Liu
    J.S.Dong
    L.Wang
    Z.J.Li
    X.T.Zhou
    L.H.Lou
    J.Zhang
    JournalofMaterialsScience&Technology, 2015, 31 (03) : 269 - 279
  • [9] Effect of Long-term Thermal Exposure on Microstructure and Stress Rupture Properties of GH3535 Superalloy
    Liu, T.
    Dong, J. S.
    Wang, L.
    Li, Z. J.
    Zhou, X. T.
    Lou, L. H.
    Zhang, J.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2015, 31 (03) : 269 - 279
  • [10] On the effect of long service exposure: changes in microstructure and mechanical properties of Ni-based superalloy
    Keyvanlou, Hassan
    Gilakjani, Reza Soleimani
    Nezakat, Majid
    METALLURGICAL RESEARCH & TECHNOLOGY, 2020, 117 (06)
12345