Fabrication of a novel cyanoethyl cellulose substrate for thin-film composite forward osmosis membrane

In this study, cyanoethyl cellulose (CEC) was used as a membrane material, and polyvinylpyrrolidone (PVP) was used as pore-forming agent to prepare the substrates for the thin-film composite (TFC) forward osmosis (FO) membrane for the first time. The experimental results demonstrate that the properties of the substrates were significantly improved after PVP was added. The scanning electron microscope (SEM) images show that a two-sublayer structure, a fringe-like top sublayer and macrovoids with sponge-like wall bottom sublayer, were formed after the addition of PVP. These improvements contributed to improved membrane performance during FO tests. Meanwhile, after adding PVP, the TFC membranes exhibited good water flux, and excellent specific reverse salt flux. For instance, the TFC-M2 exhibited 9.10/20.67 LMH water flux, 1.35/2.24 gMH reverse salt flux, and 0.15/0.11 g/L specific reverse salt flux in FO/pressure-retarded osmosis mode while using 1 M NaCl as the draw solution and deionized (DI) water as the feed solution.