Pitting corrosion of thermally aged cast duplex stainless steel for primary coolant pipes of nuclear power plants

被引：11
|
作者：
Wang, Yongqiang [1 ]
Li, Dandan [1 ]
Sun, Li [2 ]
Li, Na [2 ]
Liu, Mingkai [1 ]
Shen, Wei [1 ]
Jing, Hemin [1 ]
机构：
[1] Anhui Univ Technol, Sch Mat Sci & Engn, Maanshan 243002, Anhui, Peoples R China
[2] Anhui Univ Technol, Sch Met Engn, Maanshan, Peoples R China
来源：
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY | 2017年 / 52卷 / 06期
基金：
中国国家自然科学基金;
关键词：
Cast duplex stainless steel; thermal aging; phase; pitting corrosion; pitting potential; AGING EMBRITTLEMENT; RESISTANCE; MICROSTRUCTURE; EVOLUTION; SURFACE;
D O I：
10.1080/1478422X.2017.1325989
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The pitting corrosion of thermally aged Z3CN20.09M cast duplex stainless steel (CDSS) was investigated using potentiodynamic polarisation and electrochemical impedance spectroscopy. Both pitting potential and charge transfer resistance values of thermally aged specimens became less positive with aging time, while passive current density increased, indicating that thermal aging causes degradation in pitting corrosion resistance. The pitting potential of thermally aged specimens after annealed is higher than that of thermally aged specimens revealing that the pitting corrosion resistance of annealed specimens has been improved. The ' phase precipitation during thermal aging in ferrite brings the Cr-enriched and Cr-depleted zone microstructures which mainly induced the degradation of pitting corrosion resistance. The microsegregation of Cr element or Cr enriched and Cr-depleted zones will be alleviated or even removed due to the Cr-rich ' phases dissolution during the process of annealing. So, the pitting corrosion resistance of annealed specimens is improved.
引用
收藏
页码：447 / 452
页数：6
相关论文
共 50 条
  • [1] Localized Corrosion of Thermally Aged Cast Duplex Stainless Steel for Primary Coolant Pipes of Nuclear Power Plant
    Wang, Y. Q.
    Yang, B.
    Han, J.
    Dong, F.
    Wang, Y. L.
    [J]. IUMRS INTERNATIONAL CONFERENCE IN ASIA 2011, 2012, 36 : 88 - 95
  • [2] The Microstructure and Mechanical and Corrosion Behaviors of Thermally Aged Z3CN20-09M Cast Stainless Steel for Primary Coolant Pipes of Nuclear Power Plants
    Xue, Fei
    Shi, Fangjie
    Zhang, Chuangju
    Zheng, Qiaoling
    Yi, Dawei
    Li, Xiuqing
    Li, Yefei
    [J]. COATINGS, 2021, 11 (08)
  • [3] Pitting behavior of thermally aged Z3CN20.09M cast stainless steel for primary coolant pipe of nuclear power plant
    Chen, Yuefeng
    Chen, Bo
    Dong, Fang
    Yang, Bin
    Li, Shilei
    Yu, Xiaoyi
    [J]. ENGINEERING FAILURE ANALYSIS, 2018, 83 : 1 - 8
  • [4] Effect of Ferrite on the Precipitation of σ Phase in Cast Austenitic Stainless Steel Used for Primary Coolant Pipes of Nuclear Power Plants
    Wang, Yongqiang
    Li, Na
    [J]. MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2017, 20 (06): : 1690 - 1696
  • [5] EMBRITTLEMENT OF σ PHASE IN STAINLESS STEEL FOR PRIMARY COOLANT PIPES OF NUCLEAR POWER PLANT
    Wang Yongqiang
    Yang Bin
    Li Na
    Lin Suhua
    Sun Li
    [J]. ACTA METALLURGICA SINICA, 2016, 52 (01) : 17 - 24
  • [6] Fracture behavior of thermal aged duplex cast stainless steel for nuclear power plant
    Yao, Yuhong
    Wei, Jianfeng
    Liu, Jiangnan
    Wang, Zhengping
    Wang, Yu
    [J]. TRANSFERABILITY AND APPLICABILITY OF CURRENT MECHANICS APPROACHES, 2009, : 151 - 154
  • [7] Pitting Corrosion of Thermally Aged Duplex Stainless Steels at Different Temperature for Long Time
    Wang, Yongqiang
    Sun, Hao
    Li, Junliang
    Li, Dandan
    Li, Na
    [J]. MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2019, 22 (06):
  • [8] Microstructural Evolution and Mechanical Behavior of Thermally Aged Cast Duplex Stainless Steel
    Li, Zhenhua
    Hu, Ying
    Chen, Tao
    Wang, Xinyu
    Liu, Pan
    Lu, Yonghao
    [J]. MATERIALS, 2020, 13 (24) : 1 - 13
  • [9] Aspects of selective and pitting corrosion in cast duplex stainless steels
    Batista, SRF
    Kuri, SE
    [J]. ANTI-CORROSION METHODS AND MATERIALS, 2004, 51 (03) : 205 - 208
  • [10] Predictive model for determination of pitting corrosion in stainless steel pipes
    Riahi, M
    Alipour, R
    [J]. MATERIALS EVALUATION, 2004, 62 (03) : 373 - 375
12345