Effects of Nb on the Microstructure and Properties of Ti-Added Hypereutectic High-Cr Cast Iron

被引：5

作者：

Lai, J. P. ^{[1
]}

Pan, Q. L. ^{[1
]}

Wang, X. D. ^{[1
]}

Cui, H. R. ^{[1
]}

Sun, Y. W. ^{[1
]}

机构：

[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Hunan, Peoples R China

来源：

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2018年 / 27卷 / 09期

关键词：

cast iron; impact toughness; niobium; optical metallography; wear resistance; MECHANICAL-PROPERTIES; PRIMARY M7C3; CARBIDE; RESISTANCE; TOUGHNESS; TITANIUM;

D O I：

10.1007/s11665-018-3516-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Effects of Nb on the microstructure and properties of Ti-added hypereutectic high-Cr cast iron were studied. With the addition of Nb, a new phase (Nb,Ti)C was formed. The microstructure analysis revealed that the amount of primary carbides was decreased from 18.6 to 8.8% and the primary and eutectic carbides were greatly refined. The decrease in the amount of primary carbides was attributed with the shrinking of primary M7C3 phase zone in the phase diagram, while the refinement of primary carbides was attributed to the heterogeneous nucleus of (Nb,Ti)C phase for the primary M7C3 carbides. The macrohardness of the alloy increased from 60.8 to 63.5HRC, and the impact toughness increased from 3.8 to 5.2Jcm(-2). Furthermore, the wear resistance was enhanced with the addition of Nb due to the formation of hard (Nb,Ti)C carbides.

引用

页码：4373 / 4381

页数：9

共 50 条

[1] Effects of Nb on the Microstructure and Properties of Ti-Added Hypereutectic High-Cr Cast Iron
J. P. Lai
Q. L. Pan
X. D. Wang
H. R. Cui
Y. W. Sun
[J]. Journal of Materials Engineering and Performance, 2018, 27 : 4373 - 4381
[2] Partial Equilibrium Prediction of Solidification and Carbide Precipitation in Ti-added High Cr Cast Irons
Zhang, Hongwei
Liu, Qiang
Shibata, Hiroyuki
Wang, Qiang
Jonsson, Par
He, Jicheng
Nakajima, Keiji
[J]. ISIJ INTERNATIONAL, 2014, 54 (02) : 374 - 383
[3] Microstructure and Mechanical Properties of High-Cr Cast Iron Bars Reinforced Hadfield Steel Matrix Composites
牛立斌
[J]. Journal of Wuhan University of Technology(Materials Science), 2010, 25 (03) : 464 - 468
[4] Microstructure and Mechanical Properties of High-Cr Cast Iron Bars Reinforced Hadfield Steel Matrix Composites
Niu Libin
Xu Yunhua
Wu Hong
[J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2010, 25 (03): : 464 - 468
[5] Effects of Heat Treatment on the Microstructure and Properties of a Cast Nickel-Based High-Cr Superalloy
Lu, Hongguo
Yang, Minghui
Zhou, Li
Ma, Zhonggang
Cui, Bin
Yin, Fengshi
Li, Daoqian
[J]. METALS, 2022, 12 (12)
[6] Microstructure and mechanical properties of high-Cr cast iron bars reinforced Hadfield steel matrix composites
Libin Niu
Yunhua Xu
Hong Wu
[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2010, 25 : 464 - 468
[7] Microstructure and properties of hypereutectic high chromium cast iron containing nitrogen
Liu, Yawei
Gong, Liqiang
Dong, Minqi
Chen, Zhengyang
Jin, Tounan
Yin, Wenhang
Fu, Hanguang
[J]. MATERIALS SCIENCE AND TECHNOLOGY, 2024, 40 (01) : 26 - 41
[8] Effects of destabilization and tempering on microstructure and mechanical properties of a hypereutectic high-chromium cast iron
Abhi-Shek Jain
Muhammad Ikhmal Mustafa
Mohd Izzat Iskandar Mohd Sazili
Haiwei Chang
Ming-Xing Zhang
[J]. Journal of Materials Science, 2022, 57 : 15581 - 15597
[9] Effects of destabilization and tempering on microstructure and mechanical properties of a hypereutectic high-chromium cast iron
Jain, Abhi-Shek
Mustafa, Muhammad Ikhmal
Sazili, Mohd Izzat Iskandar Mohd
Chang, Haiwei
Zhang, Ming-Xing
[J]. JOURNAL OF MATERIALS SCIENCE, 2022, 57 (32) : 15581 - 15597
[10] Influence of Cooling Rate After Destabilization on Microstructure and Hardness of a High-Cr Cast Iron
Le Nue, Charline
Gallo, Santiago Corujeira
Vahid, Alireza
Taherishargh, Mehdi
Attar, Hooyar
Fabijanic, Daniel
Barnett, Matthew
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2024, 55 (06): : 1722 - 1727

← 1 2 3 4 5 →