Synthesis and characterization of zeolite 4A-type desiccant from kaolin

被引:14
|
作者
Du, Chunfang [1 ]
Yang, Huaming [1 ]
机构
[1] Cent S Univ, Sch Resources Proc & Bioengn, Dept Inorgan Mat, Changsha 410083, Hunan, Peoples R China
基金
中国国家自然科学基金;
关键词
Zeolite; 4A; desiccant; kaolin; water sorption capacity (WSC); final compression strength (FCS); CATALYTIC PERFORMANCE; MODIFIED ELECTRODES; ZSM-5; ZEOLITE; 4A; MEMBRANE; ASH; TRANSFORMATION; TEMPERATURE; NUCLEATION; BINDER;
D O I
10.2138/am.2010.3288
中图分类号
P3 [地球物理学]; P59 [地球化学];
学科分类号
0708 ; 070902 ;
摘要
Natural kaolin, from Fujian province in China, was used as raw material to synthesize zeolite 4A powder under low-temperature hydrothermal treatment in alkali solution. Optimization studies on various reaction parameters were conducted. With the addition of an inorganic binder (montmorillonite), the as-prepared powder was shaped into spheres for desiccant application in industrial fields. Zeolite 4A powder was characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM) and the obtained powder was a cubic phase with high crystallinity. The water sorption capacity (WSC) and final compression strength (FCS) of zeolite 4A desiccant were studied. Higher crystallinity of zeolite 4A powder led to the higher WSC of zeolite desiccant. The observed WSC and FCS of 21.0% and 44.8 N, respectively, confirmed the potential application of zeolite 4A for water sorption.
引用
收藏
页码:741 / 746
页数:6
相关论文
共 50 条
  • [1] Experimental research on synthesis of 4A-type zeolite by hydrothermal method from kaolin
    Department of Chemical Environmental Engineering, China University of Mining and Technology , Beijing 100083, China
    不详
    不详
    [J]. Rengong Jingti Xuebao, 2007, 5 (1197-1201):
  • [2] SYNTHESIS OF THE 4A-TYPE ZEOLITE FROM PRETREATED RED OPALITE
    CEKOVA, B
    ZLATANOVIC, V
    STAMBOLIEV, H
    [J]. COLLECTION OF CZECHOSLOVAK CHEMICAL COMMUNICATIONS, 1992, 57 (06) : 1218 - 1220
  • [3] Synthesis and characterization of zeolite 4A from soft kaolin
    Li, Weiwei
    Yan, Chunjie
    Hu, Wenbin
    [J]. DESALINATION AND WATER TREATMENT, 2010, 22 (1-3) : 87 - 90
  • [4] Synthesis and characterization of LTA zeolite from Kaolin Bangka
    Rahman, A.
    Purwanto, A.
    Endah, A.
    Handoko, E.
    Kusrini, E.
    Prasetyanto, E. A.
    [J]. 4TH ANNUAL APPLIED SCIENCE AND ENGINEERING CONFERENCE, 2019, 2019, 1402
  • [5] Preparation and Characterization of Zeolite type 4A using Kaolin from Ajebo, Nigeria
    Mgbemere, Henry Ekene
    Ekpe, Ikenna Christopher
    Lawal, Ganiyu
    Ovri, Henry
    Chaudhary, Anna-Lisa
    [J]. PERTANIKA JOURNAL OF SCIENCE AND TECHNOLOGY, 2019, 27 (04): : 2427 - 2438
  • [6] Easy synthesis of K-F zeolite from Kaolin, and characterization of this zeolite
    Belver, Carolina
    Vicente, Miguel Angel
    [J]. JOURNAL OF CHEMICAL EDUCATION, 2006, 83 (10) : 1541 - 1542
  • [7] Preparation of 4A-type Silver-Loaded Zeolite and Antibacterial Papers
    Zhong Zehui
    Li Ting
    Hong Ying
    [J]. GREEN PRINTING AND PACKAGING MATERIALS, 2012, 380 : 164 - 167
  • [8] Synthesis of zeolite A from Ethiopian kaolin
    Ayele, Lijalem
    Perez-Pariente, Joaquin
    Chebude, Yonas
    Diaz, Isabel
    [J]. MICROPOROUS AND MESOPOROUS MATERIALS, 2015, 215 : 29 - 36
  • [10] Conventional versus ultrasonic synthesis of zeolite 4A from kaolin
    Park, J
    Kim, BC
    Park, SS
    Park, HC
    [J]. JOURNAL OF MATERIALS SCIENCE LETTERS, 2001, 20 (06) : 531 - 533