Chemical stability and hydrogen permeation performance of Ni-BaCe0.7Y0.3-xInxO3-δ cermet membranes

The Ni-BaCe0.7Y0.3-xInxO3-delta dense cermet hydrogen separation membranes were fabricated, and the hydrogen permeability and the stability in CO2-containing atmosphere were measured. The In-doping level had a significant influence on the sinterability of the membranes and the sinterability increased with the In content increasing. The hydrogen permeation flux of the Ni-BaCe0.7Y0.3-xInx O3-delta dual phase membranes decreased with the In-doping level increasing, but the chemical stability against CO2 increased. In wet 10% CO2-containing atmospheres, the reaction between BaCe0.7 Y0.3-xInxO3-delta and CO2 made the hydrogen penetration flux decrease for the 10% and 20% In-doped membranes, while Ni-BaCe0.7In0.3O3-delta membrane showed a good long-term stability, which was evaluated as a potential alternative for hydrogen separation. (C) 2018 Elsevier B.V. All rights reserved.