Phase Structure Evolution of the Fe-Al Arc-Sprayed Coating Stimulated by Annealing

The article presents the results of research on the structural evolution of the composite Fe-Al-based coating deposited by arc spray with initial low participation of in situ intermetallic phases. The arc spraying process was carried out by simultaneously melting two different electrode wires, aluminum and low alloy steel (98.6 wt.% of Fe). The aim of the research was to reach protective coatings with a composite structure consisting of a significant participation of FexAly as intermetallic phases reinforcement. Initially, synthesis of intermetallic phases took place in situ during the spraying process. In the next step, participation of FexAly fraction was increased through the annealing process, with three temperature values, 700 degrees C, 800 degrees C, and 900 degrees C. Phase structure evolution of the Fe-Al arc-sprayed coating, stimulated by annealing, has been described by means of SEM images taken with a QBSD backscattered electron detector and by XRD and conversion electron Mossbauer spectroscopy (CEMS) investigations. Microhardness distribution of the investigated annealed coatings has been presented.