Effects of Mo additions on the glass-forming ability and magnetic properties of bulk amorphous Fe-C-Si-B-P-Mo alloys

被引：37

作者：

Jiao ZengBao ^{[1
]}

Li HongXiang ^{[1
]}

Wu Yuan ^{[1
]}

Gao JingEn ^{[1
]}

Wang ShanLin ^{[2
]}

Yi Seonghoon ^{[2
]}

Lu ZhaoPing ^{[1
]}

机构：

[1] Beijing Univ Sci & Technol, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China

[2] Kyungpook Natl Univ, Dept Mat Sci & Met, Taegu 702701, South Korea

来源：

SCIENCE CHINA-PHYSICS MECHANICS & ASTRONOMY | 2010年 / 53卷 / 03期

基金：

中国国家自然科学基金;

关键词：

Fe-based bulk metallic glass; glass-forming ability; mechanical property; magnetic property; INDUSTRIAL RAW-MATERIALS; HIGH SATURATION MAGNETIZATION; METALLIC GLASSES; HOT METAL; CRYSTALLIZATION;

D O I：

10.1007/s11433-010-0135-9

中图分类号：

O4 [物理学];

学科分类号：

0702 ;

摘要：

Glass formation, mechanical and magnetic properties of the Fe76-xC7.0Si3.3B5.0P8.7Mox (x=0, 1 at.%, 3 at.% and 5 at.%) alloys prepared using an industrial Fe-P master alloy have been studied. With the substitution of Mo for Fe, glass-forming ability (GFA) was significantly enhanced and fully amorphous rods with a diameter of up to 5 mm were produced in the alloy with 3% Mo. The Mo-containing amorphous alloys also exhibited high fracture strength of 3635-3881 MPa and excellent magnetic properties including a high saturation magnetization of 1.10-1.41 T, a high Curie temperature and a low coercive force. The unique combination of high GFA, high fracture strength and excellent magnetic properties make the newly developed bulk metallic glasses viable for practical engineering applications.

引用

页码：430 / 434

页数：5

共 50 条

[1] Effects of Mo additions on the glass-forming ability and magnetic properties of bulk amorphous Fe-C-Si-B-P-Mo alloys
YI Seonghoon
[J]. Science China(Physics,Mechanics & Astronomy), 2010, Mechanics & Astronomy)2010 (03) : 430 - 434
[2] Effects of Mo additions on the glass-forming ability and magnetic properties of bulk amorphous Fe-C-Si-B-P-Mo alloys
ZengBao Jiao
HongXiang Li
Yuan Wu
JingEn Gao
ShanLin Wang
Seonghoon Yi
ZhaoPing Lu
[J]. Science China Physics, Mechanics and Astronomy, 2010, 53 : 430 - 434
[3] Magnetic properties and glass-forming ability of modified Fe-P-Si-B bulk amorphous alloys
Lin, CY
Chin, TS
Zhou, SX
Lu, ZC
Wang, L
Chen, FF
Pan, MX
Wang, WH
[J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2004, 282 : 156 - 162
[4] Bulk glassy Fe-Mo-Ga-P-C-B-Si alloys with high glass-forming ability and good soft magnetic properties
Akiba, M
Shen, BL
Inoue, A
[J]. MATERIALS TRANSACTIONS, 2005, 46 (12) : 2773 - 2776
[5] Effect of yttrium on the glass-forming ability of Fe-Cr-Mo-C-B bulk amorphous alloys
Chen, Qingjun
Zhang, Deliang
Shen, Jun
Fan, Hongbo
Sun, Jianfei
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 427 (1-2) : 190 - 193
[6] Effects of Mo on the glass forming ability and properties of Fe-B-C-P-Si-Mo bulk metallic glasses
Wang, Ranbin
Shi, Lingxiang
Wu, You
Jia, Jili
Shao, Yang
Yao, Kefu
[J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 2024, 629
[7] The effect of P on the glass forming ability and soft magnetic properties of Co-Fe-P-Si-B-C-Mo bulk glassy alloys
Sun, Huaijun
Li, Li
Fang, Yunzhang
Wang, Linlin
Fan, Xindu
Shen, Baolong
[J]. MATERIALS LETTERS, 2015, 140 : 140 - 143
[8] High strength and good soft magnetic properties of bulk glassy Fe-Mo-Ga-P-C-B alloys with high glass-forming ability
Shen, BL
Koshiba, H
Kimura, H
Inoue, A
[J]. MATERIALS TRANSACTIONS JIM, 2000, 41 (11): : 1478 - 1481
[9] Effects of Si and Mo additions on glass-forming in FeGaPCB bulk glassy alloys with high saturation magnetization
Shen, BL
Akiba, M
Inoue, A
[J]. PHYSICAL REVIEW B, 2006, 73 (10)
[10] Influences of preparation techniques on glass-forming ability of Fe–P–B–Si–C amorphous alloys
Ji-jun Zhang
Ya-qiang Dong
Lu-yang Bie
Qiang Li
Jia-wei Li
Xin-min Wang
[J]. Journal of Iron and Steel Research International, 2018, 25 : 674 - 679

← 1 2 3 4 5 →