Characteristic of temperature change in co-deposition of Al and Fe on copper by pack cementation

被引：1
|
作者：
Su Yongkang [1 ]
Hu Guoxin [1 ]
Xu Zhengxia [1 ]
Liu Jianju [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Mech & Power Engn, Shanghai 200240, Peoples R China
来源：
THERMOCHIMICA ACTA | 2010年 / 506卷 / 1-2期
基金：
美国国家科学基金会;
关键词：
Coatings; Multilayers; Deposition process; Diffusion; ALUMINIDE COATING FORMATION; CHEMICAL-VAPOR-DEPOSITION; SURFACE COMPOSITE; KINETIC-MODEL; MICROSTRUCTURE; BEHAVIOR; ALUMINISATION; STEELS;
D O I：
10.1016/j.tca.2010.04.017
中图分类号：
O414.1 [热力学];
学科分类号：
摘要：
An experimental apparatus was set up to simulate co-deposition of Al and Fe on copper by pack cementation. The thermal history in the coating processes has been measured by K-type thermocouples. The effect of the pack mixture, holding temperature and heating rate on the temperature change on a copper surface were examined. The experimental results showed that a high Al and Fe mass fraction in pack mixture causes an obvious temperature fluctuation while the NH4Cl mass fraction and the Al2O3 mass fraction only slightly affect the temperature change. Two distinct jumps in the temperature of the sample occurred for all the experimental runs, which are strongly affected by the holding temperature. The heating rate of the pack mixture has a significant effect on the temperature change of the substrate surface. High heating rates cause an unsteady temperature change on the substrate surface. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码：67 / 72
页数：6
相关论文
共 50 条
  • [1] Co-deposition of aluminide and silicide coatings on γ-TiAl by pack cementation process
    Z. D. Xiang
    S. R. Rose
    J. S. Burnell-Gray
    P. K. Datta
    Journal of Materials Science, 2003, 38 : 19 - 28
  • [2] Co-deposition of aluminide and silicide coatings on γ-TiAl by pack cementation process
    Xiang, ZD
    Rose, SR
    Burnell-Gray, JS
    Datta, PK
    JOURNAL OF MATERIALS SCIENCE, 2003, 38 (01) : 19 - 28
  • [3] Microstructure and High Temperature Oxidation Resistance of Si-Al-Y Co-deposition Coatings Prepared on TiAl alloy by Pack Cementation Process
    Li Yong-Quan
    Xie Fa-Qin
    Wu Xiang-Qing
    Li Xuan
    JOURNAL OF INORGANIC MATERIALS, 2013, 28 (12) : 1369 - 1375
  • [4] Si-B co-deposition coatings on an Nb suicide based ultrahigh temperature alloy prepared by pack cementation technique
    Zhang, Yu
    Guo, Xiping
    ADVANCED STRUCTURAL MATERIALS, 2011, 686 : 630 - 636
  • [5] Oxidation behaviour of a MoSiBTiC alloy coated by a (Si plus B) co-deposition pack cementation method
    Nan, Xi
    Ida, Shuntaro
    Sekido, Nobuaki
    Yoshimi, Kyosuke
    Perepezko, John H.
    CORROSION SCIENCE, 2023, 214
  • [6] Microstructure and high temperature oxidation resistance of Si-Y co-deposition coatings prepared on TiAl alloy by pack cementation process
    Li, Yong-quan
    Xie, Fa-qin
    Wu, Xiang-qing
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2015, 25 (03) : 803 - 810
  • [7] Microstructure of Si-Y co-deposition coating prepared on a Nb-based ultrahigh temperature alloy by pack cementation process
    State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China
    Jinshu Xuebao, 2008, 5 (585-588):
  • [8] Microstructure of Si-Y co-deposition coating prepared on a Nb-based ultrahigh temperature alloy by pack cementation process
    Tian Xiaodong
    Guo Xiping
    ACTA METALLURGICA SINICA, 2008, 44 (05) : 585 - 588
  • [9] Microstructure and corrosion resistance of simultaneous Al-Fe coating on copper by pack cementation
    Hu Guoxin
    Xu Zhengxia
    Liu Jianju
    Li Yanhong
    SURFACE & COATINGS TECHNOLOGY, 2009, 203 (22): : 3392 - 3397
  • [10] Microstructure of Si-Cr co-deposition coatings on a Ti-Nb-Si based high temperature alloy by pack cementation process
    Qiao, Yan-Qiang
    Guo, Xi-Ping
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2010, 31 (03): : 125 - 131
12345