Preparation of β-TCP/HAP composite bioceramics

被引：2
|
作者：
Liu, Tongjun
Yang, De-An [1 ]
Di, Lizhi
机构：
[1] Tianjin Univ, Key Lab Adv Ceram & Machining Technol, Minist Educ, Tianjin 300072, Peoples R China
[2] Tianjin Med Coll, Tianjin 300052, Peoples R China
来源：
High-Performance Ceramics IV, Pts 1-3 | 2007年 / 336-338卷
关键词：
beta-TCP; bioceramics; HAP;
D O I：
10.4028/www.scientific.net/KEM.336-338.1642
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The beta-TCP granules with the range of diameter from 314 mu m to 800 mu m were prepared. The beta-TCP/HAP composite bioceramics were prepared by dipping beta-TCP discs made from the granules in HAP sol. The component and morphology of the ceramics were observed by X-ray diffraction (XRD) and scanning electron microscopy (SEM) respectively. The compressive strength of specimens was tested by Testometric M350-20KN. The results show that the samples can be calcined at 1150 degrees C without phase transformation of beta-TCP to alpha-TCP by doping the beta-TCP with 1wt% MgO. And the compressive strength of the composite ceramics reaches 24MPa.
引用
收藏
页码：1642 / 1645
页数：4
相关论文
共 50 条
  • [1] Influence of ZnO Whisker on the Agglomeration and Properties of TCP/HAP Composite Bioceramics
    Li Guanglong
    Jin Haibo
    Guo Chaobang
    Du Mingkui
    Mao Keya
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 818 - 822
  • [2] Microwave sintering of fine grained HAP and HAP/TCP bioceramics
    Veljovic, Dj.
    Zalite, I.
    Palcevskis, E.
    Smiciklas, I.
    Petrovic, R.
    Janackovic, Dj.
    CERAMICS INTERNATIONAL, 2010, 36 (02) : 595 - 603
  • [3] Study on preparation and properties of Ni3Al/HAP bioceramics composite
    Key Laboratory of Liquid Structure and Heredity of Materials Ministry of Education, Key Laboratory of Engineering Ceramics of Shandong Province, Shandong University, Jinan 250061, China
    Nongye Gongcheng Xuebao, 2006, 8 (743-746):
  • [4] Preparation of PLLA/HAP/β-TCP composite scaffold for bone tissue engineering
    Wang, Xuejun
    Lou, Tao
    Yang, Jing
    Yang, Zhen
    He, Kunpeng
    APPLIED SCIENCE, MATERIALS SCIENCE AND INFORMATION TECHNOLOGIES IN INDUSTRY, 2014, 513-517 : 143 - 146
  • [5] Fabrication of CTP/HAp novel gradient composite bioceramics
    申美玲
    赵中伟
    文士美
    陈星宇
    李洪桂
    Transactions of Nonferrous Metals Society of China, 2007, (06) : 1385 - 1390
  • [6] Fabrication of CTP/HAp novel gradient composite bioceramics
    Mei-ling, Shen
    Zhong-wei, Zhao
    Shi-mei, Wen
    Xing-yu, Chen
    Hong-gui, Li
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 (06) : 1385 - 1390
  • [7] Preparation and characterisation of ZnO/HAP bioceramics with excellent antibacterial property
    Li, Yan
    Chen, Li-Li
    Lian, Xiao-Xue
    Zhu, Jun-Wu
    MATERIALS TECHNOLOGY, 2019, 34 (07) : 415 - 422
  • [8] Fabrication and in vitro degradation behaviour of TCP/CS composite bioceramics
    Xu, Bin
    Zhang, Hanyuan
    Fang, Weijun
    BIOMEDICAL RESEARCH-INDIA, 2017, 28 (06): : 2559 - 2562
  • [9] Solid state synthesis and thermal stability of HAP and HAP – β-TCP composite ceramic powders
    R. RAMACHANDRA RAO
    H. N ROOPA
    T. S KANNAN
    Journal of Materials Science: Materials in Medicine, 1997, 8 : 511 - 518
  • [10] Ordered HAp nanoarchitecture formed on HAp-TCP bioceramics by "nanocarving" and mineralization deposition and its potential use for guiding cell behaviors
    Wang, Guocheng
    Lu, Zufu
    Zhao, Xiaobing
    Kondyurin, Alexey
    Zreiqat, Hala
    JOURNAL OF MATERIALS CHEMISTRY B, 2013, 1 (19) : 2455 - 2462
12345