Structural and mechanical study of elastomers under plane deformation

The plane shrinkage of various elastomers [natural rubber, synthetic isoprene rubber, and plasticized poly(vinyl chloride)] at room temperature has been studied via direct microscopic observations. Prior to deformation, the surface of polymer samples is decorated with a thin (several nanometers) metallic layer. Further deformation leads to formation of the surface relief in the coating. An analysis of the formed microreliefs allows one to visualize and characterize the induced stress field in the sample. The shrinkage of poly(vinyl chloride) samples is accompanied by development of the uniform surface relief over the whole surface of the deformed polymer. This fact suggests a homogeneous character of the stress field and, hence, a homogeneous structure of the polymer sample. In the case of crosslinked rubbers (natural rubber and synthetic isoprene rubber), their plane shrinkage leads to the development of an irregular pattern on the polymer surface. In addition to the folded surface relief that is typical of the poly(vinyl chloride) structure, one can observe 20-to 50-mu m "islands," which are characterized by their own morphological features. Information on structural inhomogeneity of rubbers that is obtained by scanning electron microscopy correlates with the data of DSC measurements. The advantages of electron microscopic procedure for studying structural rearrangements in polymers during strain recovery of elastomers are demonstrated.