Hydrothermally growth of TiO2 Nanorods, characterization and annealing temperature effect

Titanium dioxide TiO2 nanorods were successfully grown on conductive glass FTO substrate using the hydrothermal method at a temperature of 160 degrees C. Surface topography, structure, and optical characteristics were studied according to the influence of annealing temperature (450, 550, and 650) degrees C. The surface topography results reveal that the TiO2 had nanorods structure with a tetragonal shape, and the rod diameter increases from 84.2 nm to 116.6 nm with increasing the annealing temperature. The crystal structure of the grown TiO2 NRs exhibits a high crystallinity of polycrystalline nature with anatase and rutile phases. The preferential orientation was along (204) plane for anatase tetragonal structure. AFM image shows an intense edge, uniform surface morphology, and increased grain diameter with annealing temperature. The optical properties of TiO2 NRs were investigated, and the absorption edge shows a blue shifting as the annealing temperature increases when considering the crystallinity and morphology changes. The energy band gap was found to be lower than 3 eV, which can be attributed to the presence of anatase and rutile phases with an increment range from 2.72 to 2.86 nm alongside the increase in the annealing temperature. The results indicate that the adopted hydrothermal method and the synthesized TiO2 NRs were suitable for photovoltaic and photocatalytic applications.