Microstructure-property relations in WC-Co coatings sprayed from combinatorial Ni-plated and nanostructured powders

In this study, we addressed the effects of Ni-plating and nanostructuring of WC-Co powders on the microstructure-property relations and WC decarburization of WC-Co composite coatings. By high velocity oxygen fuel (HVOF) spraying, the coating materials were produced from four different powders, referred to as microstructured WC-Co (mc-WC), nanostructured WC-Co (nc-WC), Ni-plated microstructured WC-Co (Ni/mcWC) and Ni-plated nanostructured WC-Co (Ni/nc-WC). We found that the coatings, deposited from Ni-free powders, undergo a high level of decarburization, thereby yielding W2C phase formation in brittle amorphous W-rich Co matrix that could be preferential site for crack propagation. On the contrary, the Ni-plating treatment could reduce the amount of decarburization of the coatings, resulting in the uniform distribution of WC phase in the W-depleted Co matrix. Consequently, we revealed the underlying mechanisms responsible for WC decarburization in the coatings, and further suggested that the coating deposited from Ni-plated and nanostructured powders exhibits a superior combination of hardness and fracture toughness as compared to other coatings.