Structure and Physicomechanical Properties of the Fe3Al Intermetallic Compound Obtained by Impact Hot Compaction

被引：8
|
作者：
Tolochyn, O. I. [1 ]
Baglyuk, G. A. [1 ]
Tolochyna, O. V. [1 ]
Evych, Ya. I. [1 ]
Podrezov, Yu. M. [1 ]
Molchanovska, H. M. [1 ]
机构：
[1] Natl Acad Sci Ukraine, I Frantsevych Inst Problems Mat Sci, Kiev, Ukraine
来源：
MATERIALS SCIENCE | 2021年 / 56卷 / 04期
关键词：
intermetallic compounds; disordered structure; porosity; impact hot pressing; annealing; strength; crack resistance; IRON ALUMINIDES; VACUUM;
D O I：
10.1007/s11003-021-00456-y
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We study the influence of the conditions of impact compaction and heat treatment on the physicomechanical properties and structure of intermetallic compounds. We carried out the procedure of compaction by impact hot pressing of a Fe-14Al (wt.%) intermetallic compound prepared from iron and aluminum powders at temperatures of 1050 and 1150 degrees C, as well as the procedure of annealing of compacted specimens at 1250 degrees C for 60 min and at 1350 or 1450 degrees C for 20 min. It is shown that the procedure of impact hot pressing makes it possible to obtain practically porousless specimens at temperatures of compaction equal to 1050 degrees C and 1150 degrees C. We managed to get high-quality contacts between intermetallic particles and to improve the mechanical properties as a result of annealing at a temperature of 1350 degrees C.
引用
收藏
页码：499 / 508
页数：10
相关论文
共 50 条
  • [1] Structure and Physicomechanical Properties of the Fe3Al Intermetallic Compound Obtained by Impact Hot Compaction
    О. І. Тоlochyn
    G. А. Baglyuk
    O. V. Tolochyna
    Ya. І. Evych
    Yu. M. Podrezov
    H. M. Molchanovska
    Materials Science, 2021, 56 : 499 - 508
  • [2] The effect of Zr on the oxidation properties of Fe3Al intermetallic compound
    Przybylski, Kazimierz
    OCHRONA PRZED KOROZJA, 2009, 52 (11): : 576 - 576
  • [3] Effect of Process Conditions on the Structure and Properties of the Hot-Forged Fe3Al Intermetallic Alloy
    G. A. Baglyuk
    A. I. Tolochin
    A. V. Tolochina
    R. V. Yakovenko
    A. N. Gripachevckii
    M. E. Golovkova
    Powder Metallurgy and Metal Ceramics, 2016, 55 : 297 - 305
  • [4] On pseudoelasticity in single crystals of the intermetallic compound Fe3Al
    Brinck, A
    Engelke, C
    Neuhauser, H
    SCRIPTA MATERIALIA, 1997, 37 (05) : 569 - 574
  • [5] Effect of Process Conditions on the Structure and Properties of the Hot-Forged Fe3Al Intermetallic Alloy
    Baglyuk, G. A.
    Tolochin, A. I.
    Tolochina, A. V.
    Yakovenko, R. V.
    Gripachevckii, A. N.
    Golovkova, M. E.
    POWDER METALLURGY AND METAL CERAMICS, 2016, 55 (5-6) : 297 - 305
  • [6] Calculation of atom potentials in the intermetallic compound Fe3Al
    Zheng, Jinghong
    Cai, Zhen
    Shan, Aidang
    Shanghai Jiaotong Daxue Xuebao/Journal of Shanghai Jiaotong University, 1999, 33 (02): : 153 - 155
  • [7] Microstructure and tribology properties of hot pressing sintered Fe3Al intermetallic material
    Li, Jing
    Yin, Yansheng
    Ma, Hongtao
    Run Hua Yu Mi Feng/Lubrication Engineering, 2004, (06): : 27 - 29
  • [8] What is the true ground state of intermetallic compound Fe3Al?
    Vsianska, M.
    Sob, M.
    SOLID STATE SCIENCES, 2024, 157
  • [9] Oxidation, sulfidation and hot corrosion of intermetallic compound Fe3Al at 605°C and 800°C
    Lee, WH
    Lin, RY
    MATERIALS CHEMISTRY AND PHYSICS, 1999, 58 (03) : 231 - 242
  • [10] Mcrostrueture of Fe3Al intermetallic compound produced by plasma cladding
    Zhu, Dongmei
    Wang, Xibao
    Hanjie Xuebao/Transactions of the China Welding Institution, 2008, 29 (12): : 17 - 19
12345