Thermal diffusivity measurement of 2.25Cr-1Mo steel with internal friction

In this work, the internal friction of 2.25Cr-1Mo steel measured on a dynamic mechanical analyzer (DMA) was used to evaluate its thermal diffusivity at elevated temperatures. With the dual cantilever clamp, the internal friction of 2.25Cr-1Mo steel at high temperatures was obtained, which was mainly composed of the thermoelastic relaxation with a peak of 15 Hz and the broad spectrum of relaxation processes especially at low frequencies. According to the deconvolution of these results, the thermoelastic internal friction of 2.25Cr-1Mo steel at high temperatures was achieved. Then, the thermal diffusivity of 2.25Cr-1Mo steel at high temperatures was quantitatively estimated, which confirmed the validity of present method. (C) 2010 Elsevier B.V. All rights reserved.