Some studies on the influence of stress ratio and test temperature an X-ray fractography observations in C45 steel specimens

被引：3
|
作者：
Rajanna, K
Pathiraj, B
Kolster, BH
机构：
[1] UNIV TWENTE,FAC MECH ENGN,7500 AE ENSCHEDE,NETHERLANDS
[2] FDN ADV MET SCI,HENGELO,NETHERLANDS
来源：
ENGINEERING FRACTURE MECHANICS | 1996年 / 54卷 / 04期
关键词：
D O I：
10.1016/0013-7944(95)00242-1
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
This paper deals with additional ''X-ray fractography'' observations made on C45 steel, subsequent to the earlier work [K. Rajanna, B. Pathiraj and B. H. Kolster, Fatigue fracture surface analysis in C45 steel specimens using X-ray fractography. Engng Fracture Mech. 39, 147-157 (1991)]. Fatigue crack growth tests were carried out at 20 degrees C on CT samples prepared from this steel using different stress ratios (0.1R, 0.5R and 0.7R). Tests were also carried out at different temperatures (-20 degrees C, 20 degrees C and 115 degrees C) using a stress ratio of 0.1. The fractured surfaces were analysed for their residual stress state. The influence of the test conditions on the residual stresses developed is discussed. Copyright (C) 1996 Elsevier Science Ltd.
引用
收藏
页码：457 / 470
页数：14
相关论文
共 50 条
  • [1] FATIGUE FRACTURE SURFACE-ANALYSIS IN C45 STEEL SPECIMENS USING X-RAY FRACTOGRAPHY
    RAJANNA, K
    KOLSTER, BH
    PATHIRAJ, B
    ENGINEERING FRACTURE MECHANICS, 1991, 39 (01) : 147 - 157
  • [2] X-ray stress and residual stress analysis of Charpy steel specimens
    Hoffmann, Joachim Ernst
    Clemens, Helmut
    MATERIALPRUFUNG, 2007, 49 (11-12): : 588 - 595
  • [3] X-ray fractography under variable loading - Effect of stress ratio and maximum load
    Tsubouchi, Chiaki
    Horikawa, Takeshi
    Hattori, Yasuhira
    Zairyo/Journal of the Society of Materials Science, Japan, 2001, 50 (11) : 1207 - 1212
  • [4] X-RAY RESIDUAL-STRESS MEASUREMENTS IN NOTCHED TEST SPECIMENS
    DOWLING, NE
    HENDRICKS, RW
    RANGANATHAN, K
    JOURNAL OF TESTING AND EVALUATION, 1988, 16 (05) : 456 - 460
  • [5] SOME TECHNIQUES FOR THE GROWTH AND PREPARATION OF MICRO SPECIMENS FOR X-RAY DIFFRACTION STUDIES
    FANKUCHEN, I
    PHYSICAL REVIEW, 1945, 67 (5-6): : 197 - 197
  • [6] On the relationship between mechanical energy rate and heat dissipated rate during fatigue for a C45 steel depending on stress ratio
    De Finis, Rosa
    Palumbo, Davide
    Galietti, Umberto
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2021, 44 (10) : 2781 - 2799
  • [7] PREDICTION FOR HIGH-TEMPERATURE LOW-CYCLE FATIGUE LIFE OF AUSTENITIC STAINLESS STEEL BY X-RAY FRACTOGRAPHY.
    Nishino, Seiichi
    Sakane, Masao
    Ohnami, Masateru
    Zairyo/Journal of the Society of Materials Science, Japan, 1985, 34 (380) : 579 - 585
  • [8] X-ray investigation of a domestic refrigerator.: Observations at 25°C ambient temperature
    Inan, C
    Gonul, T
    Tanes, MY
    INTERNATIONAL JOURNAL OF REFRIGERATION-REVUE INTERNATIONALE DU FROID, 2003, 26 (02): : 205 - 213
  • [9] X-ray studies of Debye temperature of some ABO3 perovskites.
    Shebanovs, L
    FERROELECTRICS, 2002, 269 : 87 - 92
  • [10] High-temperature X-ray diffraction and spectroscopic studies of some Aurivillius phases
    Knyazev, A. V.
    Maczka, M.
    Krasheninnikova, O. V.
    Ptak, M.
    Syrov, E. V.
    Trzebiatowska-Gussowska, M.
    MATERIALS CHEMISTRY AND PHYSICS, 2018, 204 : 8 - 17
12345