Peculiarities of the MBE growth physics and technology of narrow-gap II-VI compounds

被引:37
|
作者
Sidorov, YG [1 ]
Dvoretsky, SA [1 ]
Yakushev, MV [1 ]
Mikhailov, NN [1 ]
Varavin, VS [1 ]
Liberman, VI [1 ]
机构
[1] Russian Acad Sci, Inst Semicond Phys, Siberian Branch, Novosibirsk 630090, Russia
关键词
MBE of MCT; structure of heteroepitaxial MCT; infrared photoconductor arrays;
D O I
10.1016/S0040-6090(97)00237-X
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Experimental research and a crystallochemical consideration of the chemical interaction of the film and substrate components in the A(2)B(6)/GaAs heterostructure were carried out. It was found that surface faceting, twinning and breaking of stoichiometry of the growing structure can be explained by the excess of valent electrons at the A(2)B(6)/GaAs interface. The films were grown in a multichamber mercury cadmium telluride (MCT) MBE system with different compositions of the residual gas phase in different chambers. The MCT growth chamber is equipped with a system of molecular sources of original design and a built-in automatic ellipsometer. The used system of sources allows for growing MCT films without sample rotation, uniform in composition over the substrate area of 51 mm in diameter (the composition gradient does not exceed 0.002 cm(-1)). Because there is no substrate rotation, continuous measurements of film composition can be performed during growth, and structures with specified composition over thickness can be grown. The introduction of layers with a varying energy gap into the heteroepitaxial structure increases the carrier's lifetime up to 2 mu s for x = 0.22 (77 K). A model of defects, determining the electric parameters of MBE grown films in the presence of gallium sources, is suggested. Linear photoconductor arrays for the 8-12 mu m band with background limited parameters were fabricated from the grown MCT films. (C) 1997 Elsevier Science S.A.
引用
收藏
页码:253 / 265
页数:13
相关论文
共 50 条
  • [1] MOVPE and MBE of wide gap II-VI compounds
    Gebhardt, W
    Hahn, B
    Reisinger, T
    Kastner, MJ
    Deufel, M
    BLUE LASER AND LIGHT EMITTING DIODES, 1996, : 33 - 37
  • [2] NARROW-GAP II-VI SUPERLATTICES - CORRELATION OF THEORY WITH EXPERIMENT
    MEYER, JR
    HOFFMAN, CA
    BARTOLI, FJ
    SEMICONDUCTOR SCIENCE AND TECHNOLOGY, 1990, 5 : S90 - S99
  • [3] MOVPE OF NARROW AND WIDE GAP II-VI COMPOUNDS
    MULLIN, JB
    COLEHAMILTON, DJ
    IRVINE, SJC
    HAILS, JE
    GIESS, J
    GOUGH, JS
    JOURNAL OF CRYSTAL GROWTH, 1990, 101 (1-4) : 1 - 13
  • [4] ELECTRON-DENSITY AND MOBILITY IN P-TYPE NARROW-GAP II-VI SEMICONDUCTOR COMPOUNDS
    REMESNIK, VG
    TALIPOV, NK
    SOVIET PHYSICS SEMICONDUCTORS-USSR, 1991, 25 (06): : 658 - 660
  • [5] MBE OF WIDE BANDGAP II-VI COMPOUNDS
    GUNSHOR, RL
    KOBAYASHI, M
    KOLODZIEJSKI, LA
    OTSUKA, N
    NURMIKKO, AV
    JOURNAL OF CRYSTAL GROWTH, 1990, 99 (1-4) : 390 - 398
  • [6] Local modes of transition metal ions (Mn, Fe, Co) in narrow-gap II-VI semiconductors
    Szuszkiewicz, W
    Dybko, K
    Dynowska, E
    Witkowska, B
    Jouanne, M
    Julien, C
    MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1998, 55 (1-2): : 1 - 4
  • [7] PHOTOASSISTED MBE GROWTH OF II-VI FILMS AND SUPERLATTICES
    SCHETZINA, JF
    APPLIED SURFACE SCIENCE, 1994, 79-80 : 171 - 185
  • [10] SOLUTION GROWTH OF II-VI COMPOUNDS
    AOKI, M
    WASHIYAMA, M
    NAKAMURA, H
    SAKAMOTO, K
    JAPANESE JOURNAL OF APPLIED PHYSICS, 1982, 21 (01) : 11 - 17